Título

INFLUÊNCIA DO SILÍCIO NA REDUÇÃO DO FERRO E DO ZINCO NO FERRO-GUSA

INFLUENCE OF SILICON IN THE REDUCTION OF IRON AND ZINC IN HOT METAL

Autoria

Coradini, Diego Santa Rosa; Grillo, Felipe Fardin; Sobrinho, Vicente de Paulo Ferreira Marques; Berger, Anna Paula Littig; Oliveira, Heitor Cristo Clem de; Oliveira, José Roberto de

DOI

10.5151/1982-9345-30912

Downloads

Baixar Artigo 353 Downloads

Resumo

O objetivo do trabalho é de avaliar a influência do Si na redução do Zn e do Fe da poeira, que foi adicionada na forma de briquete em gusa líquido na temperatura de 1500°C. Nos experimentos variou-se a massa de poeira e a porcentagem de silício no gusa. Para a condução dos testes, foi utilizado um forno vertical em escala laboratorial, com fluxo de gás inerte (argônio) mantido no interior do forno durante a realização dos experimentos. Todos os experimentos de fusão foram realizados no aparato experimental e utilizaram cadinhos de alumina. Periodicamente foram retiradas amostras para a verificação dos teores de carbono e silício. Verificou-se que é possível atingir valores de redução do óxido de ferro superiores a 98% para determinadas condições experimentais. Observou-se que a nova poeira coletada durante os ensaios obteve elevados teores de zinco (68% em média), além da presença de ferro.

 

The objective of the work is to evaluate the influence of Si on the reduction of Zn and Fe of the dust, which was added as briquette in hot metal at a temperature of 1500 ° C. In the experiments, the dust mass and the percentage of silicon in in the hot metal were varied. For the conduction of the tests, a vertical furnace was used in laboratorial scale, with inert gas flow (argon) kept inside the furnace during the experiments. All the experiments were performed in the experimental apparatus and used alumina crucibles. Periodically samples were collected for the verification of carbon and silicon contents. It was found that it is possible to achieve reduction values of iron oxide higher than 98% for certain experimental conditions. It was observed that the new dust collected during the tests obtained high levels of zinc (68% on average), besides the presence of iron.

Palavras-chave

Poeira de aciaria elétrica, Reciclagem, Briquetagem, Silício.

Electric steelworks dust, Recycling, Briquetting, Silicon.