Resumo
NO PRESENTE TRABALHO é ANALISADA A INFLUêNCIA DA ADIçãO DE NB NA MICROESTRUTURA E PROPRIEDADES MECâNICAS DE UM AçO C COM ALTO TEOR DE MN. PARA TAL, FOI CONDUZIDO ESTUDO EXPERIMENTAL EMPREGANDO-SE DOIS DIFERENTES AçOS CONFORME NORMA ASTM A1011/A1011M, A SABER: SS36 TIPO 2 E HSLAS50 CLASSE 1. TAIS AçOS FORAM CUIDADOSAMENTE PRODUZIDOS NA USINA DA GERDAU DE OURO BRANCO DE MODO A APRESENTAR TEORES APROXIMADOS DE C E MN, ALéM DE PROCESSADOS PELOS MESMOS PARâMETROS NA LAMINAçãO CONTROLADA DA LINHA DE TIRAS A QUENTE. ENSAIOS DE TRAçãO E ANáLISE POR MICROSCOPIA óTICA FORAM REALIZADOS EM CORPOS DE PROVA DE AMBOS OS MATERIAIS. AS ANáLISES EVIDENCIARAM QUE AMBOS OS AçOS ATENDERAM SATISFATORIAMENTE AS ESPECIFICAçõES DE PROPRIEDADES MECâNICAS DA NORMA ASTM-A1011. ADEMAIS, A MICROADIçãO DE NIóBIO EM BOBINAS DE AçO BAIXO CARBONO E ALTO MANGANêS MOSTROU-SE EFICIENTE EM PROMOVER REFINAMENTO ADICIONAL DA MICROESTRUTURA E AUMENTO SIGNIFICATIVO NAS PROPRIEDADES MECâNICAS, MAS UMA REDUçãO NA DUCTILIDADE FOI VERIFICADA.
IN THE PRESENT WORK THE INFLUENCE OF NB ADDITION ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF A C STEEL WITH HIGH MN CONTENT IS DISCUSSED. AN EXPERIMENTAL STUDY WAS CONDUCTED USING TWO DIFFERENT GRADES OF ASTM A1011/A1011M: SS36 TYPE 2 AND HSLAS50 CLASS 1 STEELS; TENSILE TESTS AND OPTICAL MICROSCOPY ANALYSIS IN SPECIMENS OF BOTH GRADES WERE PERFORMED. THE STEELS WERE CAREFULLY PRODUCED AT GERDAU PLANT IN OURO BRANCO IN ORDER TO HAVE APPROXIMATE C AND MN CONTENT AND FURTHER PROCESSED USING THE SAME PARAMETERS DURING CONTROLLED ROLLING. THE ANALYZES SHOWED THAT BOTH STEELS SATISFACTORILY MET THE MECHANICAL PROPERTIES REQUIREMENTS IN ACCORDANCE WITH ASTM-A1011 STANDARD SPECIFICATION. FURTHERMORE, NIOBIUM MICRO-ADDITION IN LOW CARBON HIGH MANGANESE STEEL COILS PROVED ITS EFFICIENCY IN PROMOTING FURTHER MICROSTRUCTURAL REFINEMENT AND MECHANICAL PROPERTIES IMPROVEMENT, BUT A REDUCTION IN DUCTILITY WAS VERIFIED.
Palavras-chave
: Nióbio; Propriedades Mecânicas; Microestrutura; Laminação Controlada
Niobium. Mechanical Properties. Microstructure. Controlled Rolling.
Como citar
CASTRO, LUCAS CARNEIRO DE;
FARIA, RICARDO JOSÉ;
SILVA, NAYARA APARECIDA NERES DA;
FLAUSINO, PAULA CIBELY ALVES.
INFLUÊNCIA DA ADIÇÃO DE NB NA MICROESTRUTURA E COMPORTAMENTO MECÂNICO DE UM AÇO C-MN
,
p. 3537-3549.
In: 77º Congresso Anual da ABM - Internacional,
São Paulo, Brasil,
2024.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-41486