Título

INFLUÊNCIA DA CICLAGEM TÉRMICA NA ESTRUTURA E CARACTERÍSTICAS DE TRANSFORMAÇÕES MARTENSÍTICAS REVERSÍVEIS DA LIGA MONOCRISTALINA Cu-13,7%Al-4,2%Ni

INFLUENCE OF THERMAL CYCLES IN THE STRUCTURE AND CHARACTERISTICS OF REVERSIBLE MARTENSITIC TRANSFORMATION OF THE MONOCRYSTALLINE Cu-13.7%Al-4.2%Ni ALLOY

Autoria

Pereira, Elaine Cristina; Matlakhova, Lioudmila Aleksandrovna; Matlakhov, Anatoliy Nikolaevich; Castilló, Teresa Ellígio; Rodríguez, Rúben J. Sánchez

DOI

10.5151/2594-5327-14757

Downloads

Baixar Artigo 43 Downloads

Resumo

No presente trabalho foi estudada uma liga monocristalina com composição nominal Cu-13,7%Al-4,2%Ni (%peso), que exibe transformações martensíticas reversíveis (TMR). A liga, fabricada pelo "Memory Crystals Group", na Rússia, foi submetida a múltiplos ciclos de aquecimento e resfriamento, num intervalo que inclui as temperaturas críticas de TMR. Neste estudo, maior atenção foi dada às alterações na estrutura e características de TMR da liga com o tratamento termo-cíclico (TTC), livre de tensões aplicadas. Na caracterização da liga foram envolvidas as análises por difração de raios-X, microscopia ótica, calorimetria diferencial e microdureza Vickers. As análises mostraram que as alterações na estrutura da liga após TTC modificam o aspecto morfológico, a microdureza, as temperaturas críticas de TMR e a participação das fases constituintes, desenvolvendo maior estabilidade da fase de alta temperatura, β1.

 

In the present work a monocrystalline Cu-13.7%Al-4.2%Ni alloy, that it exhibits reversible martensitic transformations (RMT) was investigated. The samples were submitted to thermo-cycling treatment (TCT) in interval that covers the critical temperatures associated with RMT. The alloy was produced by the firm "Memory Crystals Group", in Russia. In the study, more attention was paid to the structural changes and characteristics of RMT of the alloy after TCT. X-ray diffraction, optical microscopy, differential calorimetric analyses and microhardness Vickers were used to characterize the alloy. Analyses showed that changes in the structure of the alloy after TCT they modify morphologic aspect, microhardness, critical temperatures of RMT and the participation of the constituent phases, promoting larger stability of the high temperature β1 phase.

Palavras-chave

Liga monocristalina Cu-Al-Ni; Transformações martensíticas reversíveis; Tratamento termo-cíclico; Análise de estrutura.

Cu-Al-Ni monocrystalline alloy; Reversible martensitic transformation; Thermo-cycling treatment; Structural analyze.