INFLUÊNCIA DA DECOMPOSIÇÃO ESPINODAL NA MICROESTRUTURA E COMPORTAMENTO MECÂNICO EM DOIS AÇOS INOXIDÁVEIS DUPLEX APÓS LAMINAÇÃO A FRIO E TRATAMENTO TÉRMICO : INFLUENCE OF SPINODAL DECOMPOSITION ON MICROSTRUCTUREAND MECHANICAL BEHAVIOR IN TWO DUPLEX STAINLESS STEELS AFTER COLD ROLLING AND HEAT TREATMENT

ESTE ESTUDO INVESTIGOU OS EFEITOS DA LAMINAçãO A FRIO E DO TRATAMENTO TéRMICO NOS AçOS INOXIDáVEIS DUPLEX 2205 E 2304. AMOSTRAS FORAM SUBMETIDAS A DIFERENTES TEMPOS DE ENVELHECIMENTO A 500°C, TANTO NO ESTADO RECEBIDO QUANTO APóS LAMINAçãO A FRIO. AS MICROESTRUTURAS FORAM ANALISADAS POR MICROSCOPIA ELETRôNICA DE VARREDURA (MEV) E DIFRAçãO DE RAIOS X (DRX). O COMPORTAMENTO MECâNICO FOI ANALISADO POR MICRODUREZA VICKERS E TESTES DE TRAçãO. O PRINCIPAL OBJETIVO FOI DETECTAR A DECOMPOSIçãO ESPINODAL NAS AMOSTRAS E SUA INFLUêNCIA NAS PROPRIEDADES MECâNICAS. FORMAçãO DE MARTENSITA INDUZIDA POR DEFORMAçãO E DECOMPOSIçãO ESPINODAL FORAM OBSERVADAS NAS AMOSTRAS LAMINADAS. NA AMOSTRA 2304, A DECOMPOSIçãO ESPINODAL TAMBéM FOI OBSERVADA NO ESTADO RECEBIDO. A CARACTERIZAçãO DA DECOMPOSIçãO ESPINODAL FOI BASEADA NA APARêNCIA MARMOREADA, QUE SE TORNOU MAIS PRONUNCIADA COM TEMPOS DE RECOZIMENTO MAIS LONGOS. AO LONGO DO PROCESSO DE ENVELHECIMENTO, TANTO A DUREZA QUANTO A RESISTêNCIA à TRAçãO APRESENTARAM MELHORIAS PERCEPTíVEIS, NO ENTANTO, ISSO OCORREU à CUSTA DA REDUçãO DA DUCTILIDADE

THIS STUDY INVESTIGATED THE EFFECTS OF COLD ROLLING AND HEAT TREATMENT ON 2205 AND 2304 DUPLEX STAINLESS STEELS. SAMPLES WERE SUBJECTED TO DIFFERENT AGEING TIMES AT 500°C AS RECEIVED AND AFTER COLD ROLLING. THE MICROSTRUCTURES WERE ANALYZED BY SCANNING ELECTRON MICROSCOPY (SEM) AND X-RAY DIFFRACTION (XRD). THE MECHANICAL BEHAVIOR WAS ANALYZED BY VICKERS MICROHARDNESS AND TENSILE TESTS. THE MAIN OBJECTIVE WAS TO DETECT SPINODAL DECOMPOSITION IN THE SAMPLES AND ITS INFLUENCE ON THE MECHANICAL PROPERTIES. STRAIN-INDUCED MARTENSITE FORMATION AND SPINODAL DECOMPOSITION WERE OBSERVED IN THE ROLLED SAMPLES. IN SAMPLE 2304, SPINODAL DECOMPOSITION WAS ALSO NOTED IN THE AS-RECEIVED CONDITION. CHARACTERIZATION OF SPINODAL DECOMPOSITION WAS BASED ON THE MOTTLED APPEARANCE, WHICH BECAME MORE PRONOUNCED WITH LONGER ANNEALING TIMES. THROUGHOUT THE AGING PROCESS, BOTH HARDNESS AND TENSILE STRENGTH EXHIBITED NOTICEABLE ENHANCEMENTS, HOWEVER THIS CAME AT THE EXPENSE OF REDUCED DUCTILITY

Palavras-chave

Aço Inoxidável Duplex; Decomposição Espinodal; Microestrutura; Comportamento Mecânico

Duplex stainless steel; Spinodal decomposition; Microstructure; Mechanical behavior.

Como citar

INÁCIO, LOREN KELLY DE PAULA; SANTOS, DAGOBERTO BRANDÃO DOS; ASSUMPÇÃO, RAPHAEL FRANÇA; OLIVEIRA, ISABELA GIOVANA DE; OLIVEIRA, ANNA JULIA CASSIMIRO PRADO MITRE DE; SOUZA, SOFIA DA CRUZ; SAKAI, ARTHUR BARREIRO. INFLUÊNCIA DA DECOMPOSIÇÃO ESPINODAL NA MICROESTRUTURA E COMPORTAMENTO MECÂNICO EM DOIS AÇOS INOXIDÁVEIS DUPLEX APÓS LAMINAÇÃO A FRIO E TRATAMENTO TÉRMICO , p. 640-652. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-40552