INFLUÊNCIA DA NITROCARBONETAÇÃO EM BANHO DE SAIS SOBRE A RESISTÊNCIA À CORROSÃO DO AÇO UNS S30400 EM MEIOS CONTENDO ÍONS CLORETO

INFLUENCE OF NITROCARBURIZING IN SALT BATH OVER CORROSION STRENGTH OF UNS S30400 STAINLESS STEEL IN SOLUTIONS WITH CHLORIDE IONS

Autoria

Zanetic, Silvio Tado; Alonso-Falleiros, Neusa

DOI

10.5151/2594-5327-0033

Downloads

Baixar Artigo 24 Downloads

Resumo

Foi estudada a influência da nitrocarbonetação em banho de sais sobre a resistência à corrosão do aço inoxidável austenítico UNS S30400 solubilizado e solubilizado-sensitizado, em meios contendo íons cloreto. Inicialmente foi realizada a Pratica A (ASTM A262) e o grau de sensitização foi medido pelo método da reativação potenciodinâmica DL-EPR (Double Loop Potentiokinetic Reactivation), em seguida procedeu-se a caracterização da superfície efetuando-se exames em microscópio óptico (MO) e eletrônico de varredura (MEV), ensaios de microdureza pela DIN 50190 e análise de difração em raios X (DRX). Foram realizados ensaios de polarização potenciodinâmica cíclica em 3,5% NaCl. Os resultados mostraram que o tratamento de nitrocarbonetação foi eficiente no sentido de atingir uma dureza superficial acima de 1000 HV e promoveu à superfície do substrato uma camada espessa e uniforme. A DRX revelou a presença de nitretos

 

It was to study the influence of nitrocarburizing in salt bath over the corrosion resistance of the austenic stainless steel UNS S30400 solubilized and solubilization-sensitized, in the presence of chloride ions. First, it was evaluated the Practice A (ASTM A262) and it was measured the degree of sensitization for reaction potentiodynamic method – DL-EPR (Double Loop Potentiokinetic Reactivation), after it was evaluated the characterization of surface with realization of exams in optical and scanning electron microscopy, microhardness tests for DIN50190 and X-ray diffraction analyses (DRX). It were evaluated a cyclic potentiodynamic polarization tests with 3,5% NaCl. The results has shown that the treatment of nitrocarburizing it was efficient for reach a hardness surface over 1000HV, and produced a surface of substrate a layer thick and uniform. A DRX revealed the presence of nitriding

Palavras-chave

UNS S30400; Nitrocarbonetação em banho de sais; Cloreto.

UNS S30400, nitrocarburizing in salt bath, Pitting corrosion, chloride.