Título

INFLUÊNCIA DA TEMPERATURA DE LAMINAÇÃO A QUENTE NA MICROESTRUTURA DE NOVOS AÇOS LEVES LIGADOS AO AL E NB

INFLUENCE OF HOT ROLLING TEMPERATURE ON THE MICROSTRUCTURE OF NEW LIGHT STEEL ALLOYED WITH AL AND NB

Autoria

Jr, Eustaquio de Souza Baeta; Botelho, Ramón Alves; Aguilera, Letícia dos Santos; Araújo, Leonardo Sales; Brandão, Luiz Paulo Mendonça

DOI

10.5151/2594-5327-34682

Downloads

Baixar Artigo 10 Downloads

Resumo

OS AÇOS AVANÇADOS DE ALTA RESISTÊNCIA (AHSS) DO SISTEMA FEMNALC SÃO PRODUZIDOS VISANDO DIFERENTES COMBINAÇÕES DE MICROESTRUTURAS MULTIFÁSICAS, ENVOLVENDO NA MAIORIA DAS VEZES, FERRITAS Δ E Α, AUSTENITA (Γ), CARBONETOS E INTERMETÁLICOS, TORNANDO-SE UMA DAS CLASSES MAIS PROMISSORAS PARA UTILIZAÇÃO EM VEÍCULOS. A MAIOR PARTE DESSAS LIGAS POSSUI TEORES DE ALUMÍNIO SUFICIENTES PARA ESTABILIZAR FERRITA-Δ EM TEMPERATURA AMBIENTE E, DEVIDO AO DESENVOLVIMENTO RECENTE E POUCO EXPLORADO, A ROTA DE PRODUÇÃO DESSES MATERIAIS NÃO É COMPLETAMENTE COMPREENDIDA. ESTE TRABALHO BUSCOU VERIFICAR A MODIFICAÇÃO MICROESTRUTURAL ATRAVÉS DA LAMINAÇÃO A QUENTE DE 4 DIFERENTES LIGAS FEMNALCNB VARIANDO A TEMPERATURA DA LAMINAÇÃO DE ACABAMENTO ENTRE 900ºC E 1050ºC. AS COMPOSIÇÕES FORAM FUNDIDAS E LAMINADAS A QUENTE (ETAPAS DE DESBASTE E ACABAMENTO) E CARACTERIZADAS POR MICROSCOPIA ELETRÔNICA DE VARREDURA (MEV) E DUREZA. AS AMOSTRAS APRESENTARAM QUALIDADE DE PROCESSAMENTO COMPATÍVEL AO APRESENTADO PELA INDÚSTRIA. APESAR DE NÃO TER HAVIDO GRANDES VARIAÇÕES MICROESTRUTURAS HOUVE UMA ALTERAÇÃO SIGNIFICATIVA NA DUREZA

 

THE ADVANCED HIGH STRENGTH STEELS (AHSS) OF THE FEMNALC SYSTEM ARE PRODUCED AIMING AT DIFFERENT COMBINATIONS OF MULTIPHASE MICROSTRUCTURES, INVOLVING IN MOST CASES , AND α FERRITES, AUSTENITE (γ), CARBIDES AND INTERMETALLICS, BECOMING ONE OF THE MOST PROMISING GRADES FOR USE IN VEHICLES. MOST OF THESE ALLOYS HAVE ENOUGH ALUMINUM CONTENTS TO STABILIZE δ-FERRITE AT ROOM TEMPERATURE AND, DUE TO RECENT AND LITTLE EXPLORED DEVELOPMENT, THE PRODUCTION ROUTE OF THESE MATERIALS IS NOT COMPLETELY UNDERSTOOD. THIS WORK AIMED TO VERIFY THE MICROSTRUCTURAL MODIFICATION THROUGH HOT ROLLING OF 4 DIFFERENT FEMNALCNB ALLOYS VARYING THE TEMPERATURE OF THE FINISHING ROLLING BETWEEN 900ºC AND 1050ºC. THE COMPOSITIONS WERE MELTED AND HOT ROLLED (ROUGHING AND FINISHING STEPS) AND CHARACTERIZED BY SCANNING ELECTRON MICROSCOPY (SEM) AND HARDNESS. THE SAMPLES PRESENTED PROCESSING QUALITY COMPATIBLE WITH THAT PRESENTED BY THE INDUSTRY. ALTHOUGH THERE WERE NO LARGE VARIATIONS IN MICROSTRUCTURES, THERE WAS A SIGNIFICANT CHANGE IN HARDNESS

Palavras-chave

Aços Leves; FeMnAlC; Dureza; Laminação a Quente

Light Steels; FeMnAlC; Hardness; Hot Rolling