NA SIDERURGIA, O USO DA BIOMASSA APRESENTA-SE COMO UMA ALTERNATIVA PARA MITIGAR AS EMISSõES DE CO2 E REDUZIR O CONSUMO DE COMBUSTíVEIS NOS ALTOS-FORNOS. NESSE ESTUDO, BRIQUETES AUTORREDUTORES CONSTITUíDOS DE PELLET FEED E BAGAçO DE CANA-DE-AçúCAR TRATADO EM DIFERENTES TEMPERATURAS (250, 400 E 550ºC) FORAM PRODUZIDOS EM LABORATóRIO, OBJETIVANDO AVALIAR A INFLUêNCIA DA TEMPERATURA DE PIRóLISE DA BIOMASSA SOBRE O DESEMPENHO DESSES AGLOMERADOS QUANDO SUBMETIDOS A REGIMES TéRMICOS QUE REPRESENTAM O ALTO-FORNO. FORAM REALIZADOS ENSAIOS DE RESISTêNCIA à COMPRESSãO E QUEDA, ALéM DE ENSAIOS INTERROMPIDOS EM REGIME NãO-ISOTéRMICO E ATMOSFERA DE NITROGêNIO. TéCNICAS DE FRX E MöSSBAUER PERMITIRAM ACOMPANHAR O CONTEúDO DE FERRO E A EVOLUçãO DAS FASES NOS DIFERENTES ESTáGIOS DE AQUECIMENTO. OS RESULTADOS DEMONSTRARAM QUE OS BRIQUETES PRODUZIDOS COM BIOMASSA PIROLISADA EM TEMPERATURA MAIS ELEVADA APRESENTARAM UMA MAIOR RESISTêNCIA MECâNICA A FRIO. A PARTIR DOS ENSAIOS INTERROMPIDOS, OBSERVOU-SE UMA DIMINUIçãO DA RESISTêNCIA à COMPRESSãO COM A TEMPERATURA, ATINGINDO UM VALOR MíNIMO A 950ºC, SEGUIDO POR UM SUTIL AUMENTO A 1100ºC. OS BRIQUETES COM BIOMASSA PIROLISADA A 550ºC ALCANçARAM UM MAIOR GRAU DE METALIZAçãO, PORéM TAMBéM APRESENTARAM UM MAIOR NíVEL DE INCHAMENTO. VISANDO SEU USO EM ALTOS-FORNOS, ESSES BRIQUETES DEMONSTRARAM UM MAIOR DESEMPENHO EM TERMOS DE REDUçãO E RESISTêNCIA MECâNICA QUANDO COMPARADOS àQUELES COM BIOMASSAS PIROLISADAS EM MENORES TEMPERATURAS.
IN THE STEELMAKING, THE USE OF BIOMASS PRESENTS ITSELF AS AN ALTERNATIVE TO MITIGATE CO2 EMISSIONS AND REDUCE FUEL CONSUMPTION IN BLAST FURNACES. IN THIS STUDY, SELF-REDUCING BRIQUETTES COMPOSED OF PELLET FEED AND SUGARCANE BAGASSE TREATED AT DIFFERENT TEMPERATURES (250, 400 AND 550ºC) WERE PRODUCED IN LABORATORY, AIMING TO EVALUATE THE INFLUENCE OF THE BIOMASS PYROLYSIS TEMPERATURE ON THE PERFORMANCE OF THESE AGGLOMERATES WHEN SUBJECTED TO THERMAL REGIMES THAT REPRESENT THE BLAST FURNACE. COMPRESSIVE STRENGTH AND DROP TESTS WERE CARRIED OUT, AS WELL AS INTERRUPTED TESTS IN A NON-ISOTHERMAL REGIME AND NITROGEN ATMOSPHERE. XRF AND MöSSBAUER TECHNIQUES ALLOWED TO IDENTIFY THE IRON CONTENT AND THE EVOLUTION OF PHASES AT DIFFERENT HEATING STAGES. THE RESULTS SHOWED THAT BRIQUETTES PRODUCED WITH BIOMASS PYROLYZED AT HIGHER TEMPERATURE EXHIBITED GREATER COLD MECHANICAL STRENGTH. FROM INTERRUPTED TESTS, A DECREASE IN THE COMPRESSION STRENGTH WITH TEMPERATURE WAS OBSERVED, REACHING A MINIMUM VALUE AT 950ºC, FOLLOWED BY A SUBTLE INCREASE AT 1100ºC. BRIQUETTES WITH BIOMASS PYROLYZED AT 550ºC ACHIEVED A HIGHER METALLIZATION DEGREE, BUT ALSO SHOWED A HIGHER LEVEL OF SWELLING. FOR USE IN BLAST FURNACES, THESE BRIQUETTES DEMONSTRATED BETTER PERFORMANCE IN TERMS OF REDUCTION AND MECHANICAL STRENGTH WHEN COMPARED TO THOSE WITH BIOMASS PYROLYZED AT LOWER TEMPERATURES.
Palavras-chave
Biomassa; Pirólise; Briquete; Autorredução
Biomass; Pyrolysis; Briquette; Self-reduction.
Como citar
LEÃO, PAULA MARIA GOMES CUNHA;
ZICKER, TAÍS BIRCHAL;
ARDISSON, JOSÉ DOMINGOS;
BAGATINI, MAURÍCIO COVCEVICH.
INFLUÊNCIA DA TEMPERATURA DE PIRÓLISE DA BIOMASSA SOBRE O DESEMPENHO DE BRIQUETES AUTORREDUTORES PARA USO EM ALTOS-FORNOS
,
p. 384-397.
In: _FAUT,
São Paulo,
2000.
ISSN: -
, DOI 10.5151/Fault-41176