Título

INFLUÊNCIA DA VARIAÇÃO DE PARÂMETROS DA TÉCNICA DE FUSÃO SELETIVA A LASER NA DENSIDADE, MICROESTRUTURA E DUREZA DA LIGA RECICLADA AL-FE-CR-TI FORMADORA DE FASE QUASICRISTALINA

INFLUENCE OF SELECTIVE LASER MELTING PROCESS PARAMETERS VARIATION ON THE DENSITY, MICROSTRUCTURE AND HARDNESS OF RECYCLED QUASICRYSTALLINE FORMER AL-FE-CR-TI ALLOY

Autoria

Araujo, Aylanna Priscila Marques de; Micheloti, Leandro César; Batalha, Rodolfo Lisboa; Pauly, Simon; Kiminami, Claudio Shyinti; Gargarella, Piter

DOI

10.5151/2594-5327-34460

Downloads

Baixar Artigo 17 Downloads

Resumo

ESTE TRABALHO INVESTIGOU O EFEITO DA VELOCIDADE DE VARREDURA DO LASER, SOBREPOSIÇÃO ENTRE PISTAS, TAMANHO DA AMOSTRA E TEMPERATURA DO SUBSTRATO NA DENSIDADE, MICROESTRUTURA E DUREZA DE UMA LIGA RECICLADA, FORMADORA DE FASE QUASICRISTALINA, RICA EM ALUMÍNIO, DE COMPOSIÇÃO AL95FE2CR2TI1, QUANDO PROCESSADA PELA TÉCNICA DE FUSÃO SELETIVA A LASER. A DENSIDADE RELATIVA DAS AMOSTRAS FOI MEDIDA PELO PRINCÍPIO DE ARQUIMEDES E OS CORTES LONGITUDINAIS FORAM ANALISADOS POR MICROSCOPIA ÓPTICA (MO), MICROSCOPIA ELETRÔNICA DE VARREDURA (MEV), CALORIMETRIA DIFERENCIAL DE VARREDURA (DSC) E MICRODUREZA VICKERS (HV). A DENSIDADE RELATIVA MÉDIA DAS AMOSTRAS NÃO FOI SIGNIFICATIVAMENTE ALTERADA COM OS PARÂMETROS DE PROCESSO TESTADOS. MAIORES VELOCIDADES DE VARREDURA DO LASER RESULTARAM NUMA MAIOR FRAÇÃO DE FASES QUASICRISTALINAS E EM ESCALA MAIS REFINADA. A SOBREPOSIÇÃO DAS PISTAS TEVE MAIOR INFLUÊNCIA NA MORFOLOGIA DAS POÇAS DE FUSÃO PARA AS MENORES VELOCIDADES DE VARREDURA. A AMOSTRA PRODUZIDA EM TAMANHO MAIOR COM SUBSTRATO NÃO AQUECIDO APRESENTOU TRINCAS SUPERFICIAIS VISÍVEIS A OLHO NU. O AQUECIMENTO DO SUBSTRATO ATUOU REDUZINDO A PRESENÇA DE TRINCAS NA SUPERFÍCIE DAS PEÇAS. AS AMOSTRAS CONSTRUÍDAS COM MAIORES VELOCIDADES DO LASER RESULTARAM EM MAIORES VALORES DE MICRODUREZA E A REGIÃO DA BASE DAS AMOSTRAS SE APRESENTOU MAIS DURA QUE AS REGIÕES DE CENTRO E TOPO.

 

THIS WORK AIMED TO INVESTIGATE THE EFFECT OF THE LASER SCAN SPEED, OVERLAPPING, SIZE OF THE SAMPLE AND SUBSTRATE TEMPERATURE ON THE DENSITY, MICROSTRUCTURE AND HARDNESS OF THE RECYCLED QUASICRYSTALLINE FORMER ALLOY, RICH IN ALUMINIUM, OF THE AL95FE2CR2TI1 COMPOSITION, WHEN PROCESSED BY SELECTIVE LASER MELTING (SLM) TECHNIQUE. THE RELATIVE DENSITY OF THE SAMPLES WAS MEASURED BY ARCHIMEDES PRINCIPLE AND LONGITUDINAL SECTIONS WERE ANALYZED BY OPTICAL MICROSCOPY (OM), SCANNING ELECTRON MICROSCOPY (SEM), DIFFERENTIAL SCANNING CALORIMETRY (DSC) AND VICKERS MICROHARDNESS (HV). THE RELATIVE DENSITY OF THE SAMPLES WAS NOT SIGNIFICANTLY CHANGED WITH THE TESTED PROCESS PARAMETERS. HIGHER LASER SPEED RESULTED IN A HIGHER QUASICRYSTALLINE PHASE FRACTION AND ALSO ON A FINER SCALE. THE OVERLAPPING HAD MORE INFLUENCE IN THE MORPHOLOGY OF THE MELT POOL FOR LOWER LASER SCAN SPEED. THE SAMPLE PRODUCED IN LARGE SIZE AND USING SUBSTRATE NOT HEATED PRESENTED SUPERFICIAL CRACKS VISIBLE TO NAKED EYES. THE HEATING OF THE SUBSTRATE REDUCED THE PRESENCE OF THE CRACKS AT THE SAMPLE’S SURFACE. THE SAMPLE BUILT USING HIGHER LASER SPEED RESULTED IN HIGHER MICROHARDNESS AND THE BOTTOM OF THE SAMPLES PRESENTED THE HIGHEST HARDNESS COMPARED TO THE MIDDLE AND TOP REGIONS.

Palavras-chave

Fusão Seletiva a Laser; Liga Quasicristalina; Parâmetros de Processo; Microestrutura e microdureza

Fusão Seletiva a Laser; Liga Quasicristalina; Parâmetros de Processo; Microestrutura e microdureza