INFLUÊNCIA DE ALGUMAS VARIÁVEIS NAS PROPRIEDADES FÍSICAS DO COBALTO OBTIDO POR ELETRORRECUPERAÇÃO

INFLUENCE OF SOME VARIABLES ON PHYSICAL PROPERTIES OF COBALT OBTAINED BY ELECTROWINNING

Autoria

SOUZA, JONAS DA CRUZ TRAJANO DE; PASSOS, FABIANO AUGUSTO COSTA MAFRA; CASTRO, DANIELLE COSTAL DE; DUTRA, ACHILLES JUNQUEIRA BOURDOT

SOUZA, JONAS DA CRUZ TRAJANO DE

Eu sou esse autor

PASSOS, FABIANO AUGUSTO COSTA MAFRA

Eu sou esse autor

CASTRO, DANIELLE COSTAL DE

Eu sou esse autor

DUTRA, ACHILLES JUNQUEIRA BOURDOT

Eu sou esse autor

DOI

10.5151/2594-4711-41400

Downloads

Resumo

NESTE TRABALHO, FOI INVESTIGADA A INFLUêNCIA DO PH, DA DENSIDADE DE CORRENTE, DE IMPUREZAS E A PRESENçA DE SACO DE ANODO NAS PROPRIEDADES FíSICAS DO COBALTO OBTIDO POR ELETRORRECUPERAçãO, EM SOLUçõES DE COSO4. FORAM OBTIDAS AMOSTRAS DE COBALTO METáLICO EM QUE FORAM ANALISADOS O TAMANHO DE GRãO COM AUXíLIO DE UM MICROSCóPIO óPTICO E MICRODUREZA POR UM MICRODURôMETRO VICKERS. FORAM OBSERVADOS EFEITOS SINéRGICOS DO AUMENTO DO PH E DENSIDADE NAS PROPRIEDADES FíSICAS DAS AMOSTRAS, COM UMA REDUçãO PROGRESSIVA DA MICRODUREZA POR CONTA DO AUMENTO DO TAMANHO DE GRãO, SENDO A AMOSTRA MENOS RESISTENTE OBTIDA COM DENSIDADE DE CORRENTE DE 400 A/M² E PH 5, COM MICRODUREZA DE 169,82 HV, TAMANHO DE GRãO DE 33,01 μM. PARA O SACO DE ANODO E IMPUREZAS EM 400 A/M² E PH 4, NOTOU-SE UMA TENDêNCIA DE AUMENTO DO TAMANHO DE GRãO COM A PRESENçA DE SACO DE ANODO E O REFINO DE GRãO COM A PRESENçA DE IMPUREZAS, QUANDO CONSIDERADOS INDIVIDUALMENTE. JUNTOS, RESULTAM NA AMOSTRA MAIS REFINADA, COM 1,74 μM E 304,5 HV. A CONDIçãO MAIS ATRATIVA FOI DADA COM 400 A/M² E PH 5, PELA MELHOR UNIFORMIDADE E MAIOR DUCTILIDADE DOS DEPóSITOS, FACILITANDO O TRANSPORTE.

THE INFLUENCE OF PH, CURRENT DENSITY, IMPURITIES AND THE PRESENCE OF AN ANODE BAG ON THE PHYSICAL PROPERTIES OF COBALT OBTAINED BY ELECTROWINNING IN COSO4 SOLUTIONS WAS INVESTIGATED. COBALT METAL SAMPLES WERE OBTAINED AND THEIR GRAIN SIZE WAS ANALYZED USING AN OPTICAL MICROSCOPE AND THEIR MICROHARDNESS USING A VICKERS MICROHARDNESS TESTER. SYNERGISTIC EFFECTS OF INCREASING PH AND DENSITY ON THE PHYSICAL PROPERTIES OF THE SAMPLES WERE OBSERVED, WITH A PROGRESSIVE REDUCTION IN MICROHARDNESS DUE TO THE INCREASE IN GRAIN SIZE, WITH THE LEAST RESISTANT SAMPLE BEING OBTAINED AT A CURRENT DENSITY OF 400 A/M² AND PH 5, WITH A MICROHARDNESS OF 169.82 HV AND A GRAIN SIZE OF 33.01 μM. FOR THE ANODE BAG AND IMPURITIES AT 400 A/M² AND PH 4, THERE WAS A TENDENCY FOR THE GRAIN SIZE TO INCREASE WITH THE PRESENCE OF THE ANODE BAG AND THE GRAIN REFINEMENT WITH THE PRESENCE OF IMPURITIES, WHEN CONSIDERED INDIVIDUALLY. TOGETHER, THEY RESULT IN THE MOST REFINED SAMPLE, WITH 1.74 μM AND 304.5 HV. THE MOST ATTRACTIVE CONDITION WAS GIVEN AT 400 A/M² AND PH 5, DUE TO THE BETTER UNIFORMITY AND GREATER DUCTILITY OF THE DEPOSITS, FACILITATING TRANSPORTATION.

Palavras-chave

Cobalto; pH; Densidade de corrente; Eletrorrecuperação.

Cobalt; pH; Current density; Electrowinning.