INFLUÊNCIA DE ESTRESSES TÉRMICOS NA FIBRA DA FOLHA DO ABACAXI (ANANAS COMOSUS): INFLUENCE OF THERMAL STRESS ON PINEAPPLE LEAF FIBER (ANANAS COMOSUS)

DE MODO GERAL, AS ARGAMASSAS, RECONHECIDAS POR SUA ROBUSTEZ CONTRA COMPRESSãO E FOGO, APRESENTAM DESAFIOS COMO SUA FRAGILIDADE à TRAçãO E PROPENSãO A FISSURAS. COMO FORMA DE APRIMORAR ESSAS PROPRIEDADES, TêM-SE REALIZADO ESTUDOS FREQUENTES SOBRE A INCORPORAçãO DE FIBRAS NATURAIS COMO REFORçO CIMENTíCIO, ENTRE ESTAS FIBRAS SE ENCONTRA A FIBRA DA FOLHA DO ABACAXI. ESSAS FIBRAS, POR SEREM HIDROFíLICAS, DEMANDAM TRATAMENTOS PRéVIOS, TANTO FíSICOS QUANTO QUíMICOS, PARA SUA INCLUSãO NA MATRIZ CIMENTíCIA. ESTE ESTUDO FOCOU NA COMPARAçãO DE TRêS MéTODOS DISTINTOS DE TRATAMENTO TéRMICO DAS FOLHAS DO ABACAXI. O PROCEDIMENTO ADOTADO PARA TAL, FOI A SEPARAçãO DAS FOLHAS SEGUIDA POR TRêS CICLOS DE MOLHAGEM E SECAGEM EM DIFERENTES TEMPERATURAS: 60°C POR 24 E 48 HORAS, E 125°C POR 4 HORAS. POSTERIORMENTE, AS FOLHAS FORAM TRITURADAS EM UM PROCESSADOR NA POTêNCIA DE 900 W E FOI REALIZADO O TRATAMENTO QUíMICO DAS FIBRAS RESULTANTES COM O HIDRóXIDO DE SóDIO (5%). PARA CARACTERIZAçãO DO MATERIAL FOI REALIZADA A DIFRAçãO DE RAIOS-X E A MICROSCOPIA CONFOCAL. OS RESULTADOS INDICAM QUE O TRATAMENTO NA TEMPERATURA DE 125°C POR 4H é O MAIS EFETIVO.

IN GENERAL, MORTARS, RECOGNIZED FOR THEIR ROBUSTNESS AGAINST COMPRESSION AND FIRE, PRESENT CHALLENGES SUCH AS THEIR FRAGILITY TO TENSION AND PROPENSITY TO CRACKS. AS A WAY OF IMPROVING THESE PROPERTIES, FREQUENT STUDIES HAVE BEEN CARRIED OUT ON THE INCORPORATION OF NATURAL FIBERS AS CEMENTITIOUS REINFORCEMENT, AMONG THESE FIBERS IS PINEAPPLE LEAF FIBER. THESE FIBERS, AS THEY ARE HYDROPHILIC, REQUIRE PRIOR TREATMENTS, BOTH PHYSICAL AND CHEMICAL, FOR THEIR INCLUSION IN THE CEMENT MATRIX. THIS STUDY FOCUSED ON COMPARING THREE DIFFERENT HEAT TREATMENT METHODS FOR PINEAPPLE LEAVES. THE PROCEDURE ADOPTED FOR THIS WAS THE SEPARATION OF THE LEAVES FOLLOWED BY THREE CYCLES OF WETTING AND DRYING AT DIFFERENT TEMPERATURES: 60°C FOR 24 AND 48 HOURS, AND 125°C FOR 4 HOURS. SUBSEQUENTLY, THE LEAVES WERE CRUSHED IN A PROCESSOR AT 900 W AND THE RESULTING FIBERS WERE CHEMICALLY TREATED WITH SODIUM HYDROXIDE (5%). TO CHARACTERIZE THE MATERIAL, X-RAY DIFFRACTION AND CONFOCAL MICROSCOPY WERE PERFORMED. THE RESULTS INDICATE THAT TREATMENT AT A TEMPERATURE OF 125°C FOR 4H IS THE MOST EFFECTIVE.

Palavras-chave

Fibras naturais; Tratamento térmico; Fibra da folha do abacaxi; Resíduo agroindustrial.

Natural fibers; Heat treatment ; Pineapple fibers; Agroindustrial residue.

Como citar

FONSECA, LARISSA MENDONÇA OSORIO; JÚNIOR, JOSÉ ALEXANDRE TOSTES LINHARES; PEREIRA, IULLY DA SILVA AMARAL; MALAFAIA, SAMUEL ARAÚJO AZEVEDO; NATALLI, JULIANA FADINI; MONTEIRO, SÉRGIO NEVES; AZEVEDO, AFONSO RANGEL GARCEZ DE. INFLUÊNCIA DE ESTRESSES TÉRMICOS NA FIBRA DA FOLHA DO ABACAXI (ANANAS COMOSUS) , p. 516-524. In: 22º Enemet - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas, São Paulo, Brasil, 2024.
ISSN: 2594-4711 , DOI 10.5151/2594-4711-41313