INFLUÊNCIA DE TRATAMENTOS TERMO-CÌCLICOS NA ESTABILIDADE ESTRUTURAL DE LIGAS MONOCRISTALINAS DE Cu-Al-Ni COM EMF

INFLUENCE OF THERMAL CYCLING TREATMENTS ON STRUCTURAL STABILITY OF MONOCRYSTALLINE ALLOYS CU-AL-NI WITH SME

Autoria

Motta, Arthur da Conceição; Matlakhova, Lioudmila Aleksandrovna; Matlakhov, Anatoliy Nikolaevich; Pereira, Elaine Cristina; Toledo, Rosane; Monteiro, Sergio Neves

DOI

10.5151/2594-5327-0302

Downloads

Baixar Artigo 40 Downloads

Resumo

Neste trabalho foram estudadas duas ligas monocristalinas de Cu-Al-Ni com composições: Cu-13,5%Al-4%Ni e Cu-13,7%Al-4,2%Ni que apresentam o efeito de memória de forma (EMF). Estas ligas foram submetidas a tratamentos termo- cíclicos (TTC) até 200 ciclos de aquecimento e resfriamento, a fim de investigar sua estabilidade estrutural. A estrutura das ligas foi avaliada por microscopia ótica e difração de raios-X, a cada 100 ciclos terminando com resfriamento e aquecimento. Na liga Cu-13,5%Al-4%Ni, a estrutura com TTC terminados com o resfriamento, altera no sentido: R+B1 --> y ́1 + B1 +R-->y ́1 +B , estabilizando y ́1 , e com aquecimento, no sentido: B1 +R+(B ́1 -->y ́1 +B , também estabilizando y ́1. Na liga Cu-13,7%Al-4,2%Ni, os TTC terminados com o resfriamento, mudam a estrutura no sentido: y ́1 +R-->y ́1 -->B ́1 +(y ́1), estabilizando B ́1 , e com aquecimento no sentido: y ́1 +R+B1 -->R+(y ́1+B ́1)-->B ́ , também estabilizando B ́.

 

In this work it was studied two monocrystalline Cu-Al-Ni alloys with distinct compositions: Cu-13.5%Al-4%Ni and Cu 13.7%Al-4.2%Ni that show the shape memory effect (SME). These alloys were submitted to thermal cycling treatments (TCT) up to 200 cycles of heating and cooling in order to investigate its structural stability. The alloys’ structure was studied by optic microscopy and X-ray diffraction after each 100 cycles finishing with heating and cooling. In the Cu-13.5% Al-4%Ni alloy, the TCT finished with cooling alter the structure towards: R+B1 --> y ́1 + B1 +R-->y ́1 +B , and the same finished with heating change the structure towards: B1 +R+(B ́1 -->y ́1 +B , also stabilizing y ́1 In the Cu-13.7%Al- . 4.2%Ni, the TCT finished with cooling alter the structure towards: y ́1 +R-->y ́1 -->B ́1 +(y ́1) stabilizing B ́1 ., and the same finished with heating varies the structure towards: y ́1 +R+B1 -->R+(y ́1+B ́1)-->B ́ , also stabilizing B ́

Palavras-chave

Liga monocristalina Cu-Al-Ni; Tratamento termo-cíclico; Transformações martensíticas reversíveis; Estabilidade estrutural.

Monocrystalline Cu-Al-Ni alloy; Thermal cycling treatments; Reverse martensitic transformations; Structural stability.