PEçAS NANOESTRUTURADAS PODEM SER MODIFICADAS ATRAVéS DO PROCESSAMENTO CERâMICO, COMO ATRAVéS DO FREEZE CASTING, COM A AJUDA DE ADITIVOS COMO O POLIETILENOGLICOL (PEG). ESTE ARTIGO EXPLORA A PESQUISA EM NANOPARTíCULAS MAGNéTICAS DE FERRITAS DE ZINCO (ZNFE2O4) COMO CARGA CERâMICA PARA A PRODUçãO DE PEçAS POROSAS. FORAM UTILIZADAS TRêS VARIAçõES DE PEG’S (400, 1500 E 4000 G/MOL) COMO ADITIVO DE PROCESSAMENTO. A ANáLISE DA MORFOLOGIA DAS AMOSTRAS FOI FEITA ATRAVéS DA MICROSCOPIA ELETRôNICA DE VARREDURA (MEV) E A DENSIDADE, POROSIDADE APARENTE, MASSA ESPECíFICA APARENTE E RETRAçãO VOLUMéTRICA é ANALISADA PELA MEDIDA DE ARQUIMEDES. AS AMOSTRAS COM PEG-400 E PEG-1500 RESULTARAM EM UMA MORFOLOGIA COM UMA PIOR ORIENTAçãO E ALINHAMENTO DOS POROS. A AMOSTRA COM PEG-4000 MOSTROU-SE PROMISSORA PARA APLICAçõES COMO MATERIAIS ABSORVEDORES DE RADIAçãO ELETRôNICA, COM BAIXA RETRAçãO VOLUMéTRICA E ALTA POROSIDADE (64,6%).
NANOSTRUCTURED PARTS CAN BE MODIFIED THROUGH CERAMIC PROCESSING, SUCH AS FREEZE CASTING, WITH THE HELP OF ADDITIVES SUCH AS POLYETHYLENE GLYCOL (PEG). THIS ARTICLE EXPLORES RESEARCH INTO MAGNETIC ZINC FERRITE NANOPARTICLES (ZNFE2O4) AS A CERAMIC FILLER FOR THE PRODUCTION OF POROUS PARTS. THREE VARIATIONS OF PEG’S (400, 1500 AND 4000 G/MOL) WERE USED WITH PROCESSING ADDITIVES. THE MORPHOLOGY OF THE SAMPLES WAS ANALYZED USING SCANNING ELECTRON MICROSCOPY (SEM) AND THE DENSITY, APPARENT POROSITY, APPARENT SPECIFIC MASS AND VOLUMETRIC SHRINKAGE WERE ANALYZED USING THE ARCHIMEDES MEASURE. SAMPLES WITH PEG-400 AND PEG-1500 RESULTED IN A MORPHOLOGY WITH WORSE PORE ORIENTATION AND ALIGNMENT. THE SAMPLE WITH PEG-4000 SHOWED PROMISE FOR APPLICATIONS AS ELECTRONIC RADIATION ABSORBING MATERIALS, WITH LOW VOLUMETRIC SHRINKAGE AND HIGH POROSITY (64.6%).
Palavras-chave
Ferrita de zinco; Freeze casting; Aditivos; Taxa de resfriamento.
Zinc ferrite; Freeze casting; Additives; Cooling rate.
Como citar
FARIA, SABRINA COSTA;
RIBEIRO, JULIANA LOPES;
CARVALHO, BRUNO CRISTIAN MELLO;
MORAES, FELLIPE DE SÁ;
ALVES, DIEGO DOS SANTOS;
JÚNIOR, EUSTÁQUIO DE SOUZA BAÊTA;
AGUILERA, LETICIA DOS SANTOS.
INFLUÊNCIA DO ADITIVO DE PROCESSAMENTO NA POROSIDADE DE PEÇAS NANOESTRUTURADAS DE FERRITAS DE ZINCO
,
p. 278-288.
In: 22º Enemet - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas,
São Paulo, Brasil,
2024.
ISSN: 2594-4711
, DOI 10.5151/2594-4711-40973