INFLUÊNCIA DO NB E N NO AÇO 310 EM ALTA TEMPERATURA: UM ESTUDO MICROESTRUTURAL E MECÂNICO

INFLUENCE OF NB AND N IN 310 STEEL AT HIGH TEMPERATURE: A MICROSTRUCTURAL AND MECHANICAL STUDY

Autoria

GARCIA, JULIANNA MAGALHÃES; NUNES, THAÍSSA SAMPAIO; SOUSA, TALITA GAMA DE; BRANDAO, LUIZ PAULO MENDONÇA

GARCIA, JULIANNA MAGALHÃES

Eu sou esse autor

NUNES, THAÍSSA SAMPAIO

Eu sou esse autor

SOUSA, TALITA GAMA DE

Eu sou esse autor

BRANDAO, LUIZ PAULO MENDONÇA

Eu sou esse autor

DOI

10.5151/2594-5327-40929

Downloads

Resumo

A PESQUISA DE NOVAS LIGAS METáLICAS, COMO O AçO 310 MODIFICADO COM NITROGêNIO E NIóBIO, VISA MELHORAR A RESISTêNCIA MECâNICA DESSE AçO SEM PERDER SUAS PROPRIEDADES EM ALTAS TEMPERATURAS. NESSE ESTUDO FOI REALIZADA A AVALIAçãO MICROESTRUTURAL DO NOVO AçO 310 NBN SUBMETIDO A ENSAIOS DE TRAçãO, EM TEMPERATURA AMBIENTE E 675 °C, DE FORMA A INVESTIGAR A INFLUêNCIA DA ADIçãO DE NIóBIO E NITROGêNIO NA SUA MICROESTRUTURA E PROPRIEDADES MECâNICAS. A EVOLUçãO MICROESTRUTURAL FOI ESTUDADA ATRAVéS DE MICROSCOPIA ELETRôNICA DE VARREDURA. FOI VERIFICADO A FORMAçãO DE COMPOSTOS DE NBC E NBN QUE REFORçAM A MATRIZ AUSTENíTICA. OS RESULTADOS DOS ENSAIOS DE TRAçãO REVELAM UM AUMENTO SIGNIFICATIVO NO LIMITE DE ESCOAMENTO, NA RESISTêNCIA à TRAçãO E NO ALONGAMENTO EM TEMPERATURAS ELEVADAS, DEMONSTRANDO A CAPACIDADE DESSES ELEMENTOS EM MANTER A RESISTêNCIA MECâNICA DO MATERIAL. ALéM DISSO, A ANáLISE DAS SUPERFíCIES DE FRATURA REVELA DIFERENTES MECANISMOS DE FRATURA DúCTIL NAS SUAS TEMPERATURAS

THE RESEARCH ON NEW METAL ALLOYS, SUCH AS NITROGEN AND NIOBIUM-MODIFIED 310 STEEL, AIMS TO ENHANCE THE MECHANICAL STRENGTH OF THIS STEEL WITHOUT COMPROMISING ITS PROPERTIES AT HIGH TEMPERATURES. IN THIS STUDY, MICROSTRUCTURAL EVALUATION OF THE NEW 310NBN MODIFIED STEEL WAS CONDUCTED THROUGH TENSILE TESTS AT ROOM TEMPERATURE AND 675°C TO INVESTIGATE THE INFLUENCE OF NIOBIUM AND NITROGEN ADDITION ON ITS MICROSTRUCTURE AND MECHANICAL PROPERTIES. THE MICROSTRUCTURAL EVOLUTION WAS STUDIED USING SCANNING ELECTRON MICROSCOPY. THE FORMATION OF NBC AND NBN COMPOUNDS THAT REINFORCE THE AUSTENITIC MATRIX WAS OBSERVED. THE RESULTS OF THE TENSILE TESTS REVEAL A SIGNIFICANT INCREASE IN YIELD STRENGTH, TENSILE STRENGTH, AND ELONGATION AT ELEVATED TEMPERATURES, DEMONSTRATING THE ABILITY OF THESE ELEMENTS TO MAINTAIN THE MECHANICAL STRENGTH OF THE MATERIAL. ADDITIONALLY, THE ANALYSIS OF THE FRACTURE SURFACES REVEALS DIFFERENT DUCTILE FRACTURE MECHANISMS AT THESE TEMPERATURES

Palavras-chave

Aço 310; NbC; NbN; Resistência mecânica

310 steel; NbC; NbN; Mechanical resistance.