ISSN 2594-5297
57° Seminário de Laminação e Conformação de Metais — vol. 57, num.57 (2022)
Título
Autoria
DOI
Downloads
Resumo
O MAGNÉSIO TEM UM NÚMERO LIMITADO DE SISTEMAS DE DESLIZAMENTO PARA ACOMODAR A DEFORMAÇÃO PLÁSTICA. DEVIDO A SUA LIMITADA DUCTILIDADE, É MAIS DIFÍCIL FABRICAR COMPONENTES ESTRUTURAIS DESTE MATERIAL. UMA DAS SOLUÇÕES PROPOSTAS PARA CONTORNAR ESSA LIMITAÇÃO É A UTILIZAÇÃO DE PROCESSOS ECAE, QUE PERMITEM O CONTROLE E MODIFICAÇÃO DE DUAS CARACTERÍSTICAS DETERMINANTES DAS PROPRIEDADES DE RESISTÊNCIA E DUCTILIDADE DO MAGNÉSIO: O TAMANHO DO GRÃO E A TEXTURA CRISTALOGRÁFICA. NESSE CONTEXTO, O MAGNÉSIO COMERCIALMENTE PURO FOI PROCESSADO POR ECAE À TEMPERATURA CONSTANTE DE 300 °C, DE 1 A 4 PASSAGENS, SEGUINDO A ROTA BC. ALÉM DISSO, SIMULAÇÕES UTILIZANDO O MODELO VPSC FORAM REALIZADAS E COMPARADAS COM OS DADOS EXPERIMENTAIS. ESTE TRABALHO AVALIA A INFLUÊNCIA DO PROCESSO ECAE NA MICROESTRUTURA E TEXTURA CRISTALOGRÁFICA DO MG, AVALIANDO A CONCORDÂNCIA ENTRE OS RESULTADOS SIMULADOS E EXPERIMENTAIS. ASSIM, A MICROESTRUTURA COM MENOR DIÂMETRO DE GRÃO E MELHOR UNIFORMIDADE FOI OBSERVADA APÓS TRÊS PASSES. EM RELAÇÃO À TEXTURA CRISTALOGRÁFICA EXPERIMENTAL, HOUVE UMA EVOLUÇÃO GRADATIVA ATÉ O PROCESSAMENTO EM 4 PASSES. EM CONCLUSÃO, OS TESTES DE TEXTURA CRISTALOGRÁFICA SIMULADA CORRESPONDENTES A 4 PASSES COINCIDIRAM COM O RESULTADO OBTIDO EXPERIMENTALMENTE.
MAGNESIUM HAS A LIMITED NUMBER OF SLIP SYSTEMS TO ACCOMMODATE PLASTIC DEFORMATION. HENCE ITS LIMITED DUCTILITY, IT IS MORE DIFFICULT TO MANUFACTURE STRUCTURAL COMPONENTS OF THIS MATERIAL. ONE OF THE SOLUTIONS THAT HAVE BEEN PROPOSED TO OVERCOME THIS LIMITATION IS THE USE OF ECAE PROCESSES, WHICH ALLOW THE CONTROL AND MODIFICATION OF TWO DETERMINANT CHARACTERISTICS FOR THE STRENGTH AND DUCTILITY MAGNESIUM PROPERTIES: GRAIN SIZE AND CRYSTALLOGRAPHIC TEXTURE. IN THIS CONTEXT, COMMERCIALLY PURE MAGNESIUM WAS PROCESSED BY ECAE AT 300 °C CONSTANT TEMPERATURE, FROM 1 TO 4 PASSES, FOLLOWING THE BC ROUTE. BESIDES, SIMULATIONS USING THE VPSC MODEL WERE PERFORMED AND COMPARED WITH THE EXPERIMENTAL DATA. THIS WORK EVALUATES THE ECAE PROCESS’S INFLUENCE ON THE MICROSTRUCTURE AND CRYSTALLOGRAPHIC TEXTURE OF MG BY EVALUATING THE AGREEMENT BETWEEN SIMULATED AND EXPERIMENTAL RESULTS. THUS, THE MICROSTRUCTURE WITH SMALLER GRAIN DIAMETER AND BETTER UNIFORMITY WAS OBSERVED AFTER THREE PASSES. REGARDING THE EXPERIMENTAL CRYSTALLOGRAPHIC TEXTURE, THERE WAS A GRADUAL EVOLUTION UNTIL PROCESSING IN 4 PASSES. IN CONCLUSION, THE SIMULATED CRYSTALLOGRAPHIC TEXTURE TESTS CORRESPONDING TO 4 PASSES COINCIDED WITH THE RESULT OBTAINED EXPERIMENTALLY.
Palavras-chave
EXTRUSÃO ANGULAR POR CANAIS IGUAIS; MAGNÉSIO; TEXTURA CRISTALOGRÁFICA; VPSC
Equal channel angular extrusion; Magnesium; Crystallographic Texture; VPSC.
Como citar
Saraiva, Breno Rabelo Coutinho;
Neto, João Rodrigues de Barros;
Filho, José Amilton Cardoso de Oliveira;
Leão, Pablo Bruno Paiva;
Gömes, Francisco Bruno Alexandre;
Leiva, Daniel Rodrigo;
Abreu, Hamilton Ferreira Gomes de.
INFLUÊNCIA DO NÚMERO DE PASSES DE ECAE NA MICROESTRUTURA E NA TEXTURA CRISTALOGRÁFICA DO MAGNÉSIO: EXPERIMENTOS E SIMULAÇÕES
,
p. 255-265.
In: 57° Seminário de Laminação e Conformação de Metais,
São Paulo,
2022.
ISSN: 2594-5297
, DOI 10.5151/2594-5297-34591