Título

INFLUÊNCIA DO TAMANHO E FORMA DO PÓ DA CASCA DO COCO NA DILATOMETRIA DE COMPÓSITOS PARTICULADOS

INFLUENCE OF THE SIZE AND SHAPE OF THE LOAD ON THE LINEAR THERMAL EXPANSION OF PARTICULATED COMPOSITES

Autoria

Velasco, David Coverdale Rangel; Simonassi, Noan Tonini; Lopes, Felipe Perissé Duarte; Vieira, Carlos Maurício Fontes; Delaqua, Geovana Carla Girondi

DOI

10.5151/2594-5327-34654

Downloads

Baixar Artigo 13 Downloads

Resumo

VISANDO OBTER NOVOS MATERIAIS, O HOMEM COMEÇOU A COMBINAR DIFERENTES TIPOS DE MATERIAIS, CRIANDO ASSIM COMPÓSITOS. ESTES, PODEM POSSUIR NÃO SÓ PROPRIEDADES E CUSTOS MAIS ATRATIVOS QUE OS MATERIAIS CONVENCIONAIS, MAS TAMBÉM GERAR BENÉFICOS AMBIENTAIS COMO MINIMIZAR O CONSUMO DE RECURSOS NATURAIS E APROVEITAR RESÍDUOS QUE EM OUTRORA SERIAM DESCARTADOS. NESTE SENTIDO, ESTE TRABALHO TEM POR OBJETIVO CARACTERIZAR A EXPANSÃO TÉRMICA LINEAR DE COMPÓSITOS REFORÇADOS COM PARTICULADOS DA CASCA DE COCO EM DUAS CONFIGURAÇÕES, PROCESSADOS E NÃO PROCESSADOS. OS PARTICULADOS PROCESSADOS FORAM MOÍDOS POR 24 HORAS EM UM MOINHO DE BOLAS DA MARCA SERVITECH, MODELO CT-240/A. OS ENSAIOS FORAM REALIZADOS EM UM DILATÔMETRO DA MARCA NETZSCH, MODELO DIL 402 PC, A UMA TAXA DE 2°C/MIN, VISANDO CARACTERIZAR O COMPORTAMENTO DE 30 A 190°C. POR MEIOS DOS ENSAIOS FOI POSSÍVEL CARACTERIZAR O COMPORTAMENTO DOS COMPÓSITOS, BEM COMO OBSERVAR O QUE O COMPORTAMENTO DOS COMPÓSITOS VARIOU DE ACORDO COM A QUANTIDADE DE CARGA, DE MANEIRA NÃO PROPORCIONAL, E TIPO DE CARGA. ACRESCENTA-SE AINDA QUE O PROCESSAMENTO DOS PARTICULADOS FAVORECE A REDUÇÃO DAS TENSÕES INTERNAS, INFLUINDO MENOS QUE OS PARTICULADOS NÃO PROCESSADOS NA DILATAÇÃO DO EPÓXI.

 

IN ORDER TO OBTAIN NEW MATERIALS, MAN BEGAN TO COMBINE DIFFERENT TYPES OF MATERIALS, THUS CREATING COMPOSITES. THESE CAN NOT ONLY HAVE PROPERTIES AND COSTS MORE ATTRACTIVE THAN CONVENTIONAL MATERIALS, BUT ALSO GENERATE ENVIRONMENTAL BENEFITS SUCH AS MINIMIZING THE CONSUMPTION OF NATURAL RESOURCES AND TAKING ADVANTAGE OF WASTE THAT WOULD ONCE HAVE BEEN DISCARDED. IN THIS SENSE, THIS WORK AIMS TO CHARACTERIZE THE LINEAR THERMAL EXPANSION OF COMPOSITES REINFORCED WITH COCONUT SHELL PARTICLES IN TWO CONFIGURATIONS, PROCESSED AND UNPROCESSED. THE PROCESSED PARTICLES WERE GROUND FOR 24 HOURS IN A BALL MILL OF THE BRAND SERVITECH, MODEL CT-240 / A. THE TESTS WERE PERFORMED ON A NETZSCH DILATOMETER, MODEL DIL 402 PC, AT A RATE OF 2°C/MIN, AIMING TO CHARACTERIZE THE BEHAVIOR OF 30 TO 190°C. THROUGH THE TESTS IT WAS POSSIBLE TO CHARACTERIZE THE BEHAVIOR OF THE COMPOSITES, AS WELL AS TO OBSERVE WHAT THE BEHAVIOR OF THE COMPOSITES VARIED ACCORDING TO THE AMOUNT OF LOAD, IN A NON-PROPORTIONAL WAY, AND TYPE OF LOAD. IT IS ALSO ADDED THAT THE PROCESSING OF PARTICULATES FAVORS THE REDUCTION OF INTERNAL STRESSES, INFLUENCING LESS THAN UNPROCESSED PARTICLES IN THE EXPANSION OF THE EPOXY.

Palavras-chave

Compósitos particulados; Dilatometria linear; Epóxi; Pó da casca de coco

Particulate composites; Linear dilatometry; Epoxy; Coconut shell powder