INFLUÊNCIA DO TRATAMENTO TÉRMICO DE TÊMPERA EM DISTINTAS TEMPERATURAS NA MICROESTRUTURA DE UM AÇO COM ADIÇÃO DE AL E NB

QUENCHING HEAT TREATMENT INFLUENCE ON DIFFERENT TEMPERATURES IN A STEEL MICROSTRUCTURE WITH AL AND NB ADDITION

DOI

10.5151/2594-5327-33598

Downloads

Baixar Artigo 19 Downloads

Resumo

As diversas aplicações de materiais metálicos fazem com que essa área esteja em constante desenvolvimento, sendo a indústria automobilística um setor que promove diversos desafios para a indústria siderúrgica. A partir dessas pesquisas foram desenvolvidos diversos materiais dentre eles aços assistidos pelo efeito da plasticidade induzida pela transformação (TRIP). Recentemente foram observados em aços com alto teor de alumínio características bem interessantes, que necessitam de melhor entendimento. Sendo assim esse trabalho avalia a influência do tratamento térmico de têmpera, com distintas temperaturas de encharque, em uma liga com alto teor de alumínio e adição de nióbio através de microscopia óptica e análises de difração de Raios X. A partir dos resultados obtidos verificou-se que quanto mais elevada a temperatura de encharque empregada no tratamento térmico, maiores os percentuais de martensita formados na microestrutura, indicando que o encharque deu-se em um campo intercrítico de coexistência de austenita e ferrita, e que há um consumo na fração de ferrita pró-eutetóide pré-existente que contribui para o empobrecimento em elementos de ligas da austenita e menor fração de austenita retida associada ao constituinte martensita-austenita (MA).

 

The diverse applications of metallic materials make this area in constant development, being the automobile industry a sector that promotes several challenges for the steel industry. From this research were developed several materials among them steels assisted by the transformation induced plasticity (TRIP) effect. It has recently been observed in steels containing high aluminum the possibility of very interesting characteristics that need a greater understanding. Thus, this work evaluates the influence of quenching heat treatment, with distinct soaking temperatures, on steel with high aluminum content and niobium addition through optical microscopy and X-ray diffraction analysis. From the results obtained, it was verified that the higher the soaking temperature applied in heat treatment higher the martensite formed percentage in the microstructure, indicating that the soaking took place in an intercritical field of austenite and ferrite coexistence and that there is a consumption in the pro-eutectoid ferrite fraction pre-existent that contributes to the alloy elements impoverishment in austenite and a smaller retained austenite fraction associated to the martensite-austenite (MA) constituent.

Palavras-chave

Aços TRIP; Caracterização microestrutural; DRX.

TRIP STEELS; MICROSTRUCTURAL CHARACTERIZATION; XRD

Como citar

Gurgel, Mônica Aline Magalhães; Nunes, Larissa Fernandes; Júnior, Eustáquio de Souza Baêta; Botelho, Ramón Alves; Araújo, Leonardo Sales; Brandão, Luiz Paulo Mendonça; Paula, Andersan dos Santos. INFLUÊNCIA DO TRATAMENTO TÉRMICO DE TÊMPERA EM DISTINTAS TEMPERATURAS NA MICROESTRUTURA DE UM AÇO COM ADIÇÃO DE AL E NB , p. 2086-2097. In: 74º Congresso Anual da ABM, São Paulo, 2019.