Título

INFLUÊNCIA DOS ÍONS DE CLORETO SOBRE A RESISTÊNCIA A CORROSÃO DO AÇO INOXIDÁVEL DUPLEX S31803

INFLUENCE OF CHLORIDE IONS ON THE CORROSION RESISTANCE OF DUPLEX S31803 STAINLESS STEEL

Autoria

Souza, Lucas Menezes de

Souza, Lucas Menezes de

Eu sou esse autor

DOI

10.5151/2594-5327-34147

Downloads

Resumo

NESTE TRABALHO FOI AVALIADA A INFLUÊNCIA DO MEIO CORROSIVO E DA TEMPERATURA NAS PROPRIEDADES DE RESISTÊNCIA À CORROSÃO DO AÇO INOXIDÁVEL DUPLEX S31803. O PROCESSO CORROSIVO FOI REALIZADO UTILIZANDO SOLUÇÃO DE ÁCIDO CLORÍDRICO 1,5%, À 25, 50 E 80 °C, QUE É UMA SOLUÇÃO TÍPICA QUANDO SE DESEJA AVALIAR A CORROSÃO PUNTIFORME, POR ENVOLVER ÍONS DE CLORETO. A MICROESTRUTURA DA AMOSTRA CONFORME RECEBIDA FOI ANALISADA ANTES E APÓS PROCESSO CORROSIVO UTILIZANDO AS TÉCNICAS DE MICROSCOPIA ÓTICA, CONFOCAL. EM SEGUIDA, FORAM REALIZADOS OS ENSAIOS MECÂNICOS E DE RESISTÊNCIA À CORROSÃO. A MICROESTRUTURA DO AÇO INOXIDÁVEL DUPLEX S31803 É COMPOSTA DE DUAS FASES, FERRITA E AUSTENITA, ORIENTADAS NO SENTIDO DE LAMINAÇÃO, COM UM BALANÇO APROXIMADO DE 50% EM VOLUME DAS FRAÇÕES DE FASES PRESENTES. O MEIO CORROSIVO DE HCL, NAS TEMPERATURAS DE 25 E 50 °C, PROPORCIONOU O DESENVOLVIMENTO DA CORROSÃO UNIFORME E DA CORROSÃO POR PITES NO MATERIAL, O QUE É TÍPICO DE SOLUÇÕES CONTENDO ÍONS DE CLORETOS. COM O AUMENTO DA TEMPERATURA ATÉ 80 °C, FOI OBSERVADO A DETERIORAÇÃO DO FILME PASSIVO, AUMENTANDO EXPRESSIVAMENTE A CORROSÃO UNIFORME, ONDE ESTÁ SE DESENVOLVEU DE FORMA SELETIVA, TENDO A FERRITA COMO ANODO E A AUSTENITA COMO CATODO. AS AMOSTRAS QUANDO SUBMETIDAS AOS MEIOS CORROSIVOS E AS DIFERENTES TEMPERATURAS, TENDEM A DIMINUIR SEUS VALORES DE PROPRIEDADES MECÂNICAS QUANDO SOFREM A CORROSÃO PUNTIFORME. EM CONTRAPARTIDA QUANDO A CORROSÃO UNIFORME FOI VERIFICADA NAS AMOSTRAS, A TENDÊNCIA FOI TER UM AUMENTO NOS VALORES DAS PROPRIEDADES MECÂNICAS QUANDO COMPARADO COM O ESTADO INICIAL

IN THIS WORK, THE INFLUENCE OF THE CORROSIVE MEDIUM AND TEMPERATURE ON THE CORROSION RESISTANCE PROPERTIES OF S31803 DUPLEX STAINLESS STEEL WAS EVALUATED. THE CORROSIVE PROCESS WAS CARRIED OUT USING A 1.5% HYDROCHLORIC ACID SOLUTION, AT 25, 50 AND 80 ° C, WHICH IS A TYPICAL SOLUTION WHEN IT IS DESIRED TO EVALUATE POINT CORROSION, AS IT INVOLVES CHLORIDE IONS. THE MICROSTRUCTURE OF THE SAMPLE AS RECEIVED WAS ANALYZED BEFORE AND AFTER THE CORROSIVE PROCESS USING THE TECHNIQUES OF OPTICAL MICROSCOPY, CONFOCAL. THEN, MECHANICAL AND CORROSION RESISTANCE TESTS WERE PERFORMED. THE MICROSTRUCTURE OF S31803 DUPLEX STAINLESS STEEL IS COMPOSED OF TWO PHASES, FERRITE AND AUSTENITE, ORIENTED IN THE LAMINATION DIRECTION, WITH AN APPROXIMATE BALANCE OF 50% IN VOLUME OF THE PHASE FRACTIONS PRESENT. THE CORROSIVE MEDIUM OF HCL, AT TEMPERATURES OF 25 AND 50 ° C, ALLOWED THE DEVELOPMENT OF UNIFORM CORROSION AND PITTING CORROSION IN THE MATERIAL, WHICH IS TYPICAL OF SOLUTIONS CONTAINING CHLORIDE IONS. WITH THE INCREASE IN TEMPERATURE TO 80 ° C, DETERIORATION OF THE PASSIVE FILM WAS OBSERVED, SIGNIFICANTLY INCREASING UNIFORM CORROSION, WHERE IT IS DEVELOPED SELECTIVELY, WITH FERRITE AS AN ANODE AND AUSTENITE AS CATHODE. SAMPLES, WHEN SUBJECTED TO CORROSIVE MEDIA AND DIFFERENT TEMPERATURES, TEND TO DECREASE THEIR VALUES ​​OF MECHANICAL PROPERTIES WHEN THEY UNDERGO PUNCTIFORM CORROSION. ON THE OTHER HAND, WHEN UNIFORM CORROSION WAS OBSERVED IN THE SAMPLES, THE TENDENCY WAS TO INCREASE THE VALUES ​​OF MECHANICAL PROPERTIES WHEN COMPARED TO THE INITIAL STATE.

Palavras-chave

DUPLEX; CORROSÃO; PITES

duplex; corrosion; pites