MAPAS DE DESGASTE MICROABRASIVO DO AÇO INOXIDÁVEL AUSTENÍTICO AISI 316L: UMA ANÁLISE COMPARATIVA DE SUPERFÍCIES NÃO NITRETADAS E NITRETADAS A PLASMA

MICRO-ABRASION WEAR MAPPING FOR AISI 316L STAINLESS STEEL: A COMPARATIVE ANALYSIS ON UNTREATED AND PLASMA NITRIDED SURFACES

DOI

10.5151/1516-392X-24219

Downloads

Baixar Artigo 426 Downloads

Resumo

Os modos de desgaste de um material podem sofrer transições decorrentes de alterações nas condições do tribossistema. Para o estudo e análise dos fenômenos associados às eventuais mudanças, a técnica de micro-abrasão do tipo esfera livre é reconhecidamente uma boa escolha. No presente trabalho, para o aço inoxidável austenítico AISI 316L, fez-se um estudo do comportamento da taxa de desgaste, bem como do mecanismo de desgaste em função da carga de ensaio, tipo de abrasivo (SiO2 ou SiC), dureza do material (modificada pela sua nitretação) e concentração de abrasivo. O desgaste por deslizamento predomina quando a lama abrasiva é constituída de SiO2, enquanto o rolamento passa a prevalecer com a troca do abrasivo para o SiC. Verificou-se que em nenhum dos dois casos ocorreu transição de mecanismos após variações nas condições de ensaio. Por outro lado, o coeficiente de desgaste do material aumenta com a carga de ensaio, substituição do SiO2 pelo SiC e tende a cair com a nitretação (aumento de dureza) do aço e com a concentração de abrasivo. O aumento simultâneo da carga de ensaio e da concentração de sílica na lama diminui significativamente a taxa de desgaste, encurtando o período de "running-in".

 

The transition in the wear mechanisms of a material can occur owing to changes on the tribosystem conditions. “Free ball” micro-scale abrasion method is widely used for studying the associated phenomena. In this work, the behavior of both the wear coefficient and wear mechanism for the 316 stainless steel was studied as a function of the testing load, abrasive (SiC or SiO2) as well their concentration in the slurry, and material hardness (untreated and plasma nitrided). Grooving wear was found to be dominant when using SiO2 slurries, whereas wear in SiC slurries is dominated by the mechanism of rolling. In spite of no transition in the wear mechanisms when changed the testing conditions, it was found a trend in the wear coefficient to increase whether at high loads or replacing SiO2 by SiC, and to fall down when the steel is nitrided (hardened) and low slurry concentrations are used. A decreasing in both the wear coefficient and "running-in" step was observed when the testing load and SiO2 concentration are simultaneously increased.

Palavras-chave

Desgaste microabrasivo; Mapas de desgaste; Aço inoxidável austenítico AISI 316L

Micro-scale abrasion wear; Wear maps; AISI 316L austenitic stainless steel

Como citar

João Paulo Calixto da Silva; Cherlio Scandian; Adonias Ribeiro Franco Júnior. MAPAS DE DESGASTE MICROABRASIVO DO AÇO INOXIDÁVEL AUSTENÍTICO AISI 316L: UMA ANÁLISE COMPARATIVA DE SUPERFÍCIES NÃO NITRETADAS E NITRETADAS A PLASMA , p. 5915-5925. In: 69° Congresso Anual da ABM - Internacional, São Paulo - Brasil, 2014.