In order to study the metallic coating deposition obtained through High Velocity Oxygen Fuel (HVOF) thermal spraying process of the materials STELLIT 6 PM SD 38 EF, 97 MXC, 140 MXC, 1342 VM, 1350 VM and 8812, an adhesion testing device was built in accordance with ASTM C 633-79 standard. This standard is often used as a method of establishing the influence of spraying, the substrate’s surface and the abrasive spray gun conditions, coating thickness, and other quality factors. Metallography, hardness and fracture surface analysis were performed. The fracture surface analysis revealed many results. In another words, they showed different fracture types: cohesive, adhesion and adhesive fracture.
Para estudo de processos de deposição de revestimentos metálicos obtidos através do processo de aspersão térmica chama combustível de alta velocidade (HVOF) dos materiais STELLIT 6 PM SD 38 EF, 97 MXC, 140 MXC, 1342 VM, 1350 VM e 8812, foi construído um dispositivo de ensaio de adesão através da norma ASTM C 633- 79, usado freqüentemente como uma ferramenta para determinar a influência das condições de aspersão, da superfície do substrato e do jateamento abrasivo, espessura do revestimento, além de outros fatores da qualidade. Foi realizado ensaios de dureza, metalografia e análise da superfície de fratura. As análises das superfícies de fratura revelaram resultados variados, ou seja, apresentaram diferentes tipos de fratura: fraturas coesivas, aderência e fratura adesiva.
Palavras-chave
Thermal spraying; HVOF; Adhesion testing device.
Aspersão térmica; HVOF; Dispositivo para ensaio de aderência.
Como citar
Varavallo, Rogério;
Manfrinato, Marcos Dorigão;
Rossino, Luciana Sgarbi;
Camargo, Flavio;
Maluf, Omar.
METALLIC COATING ADHESION OBTAINED THROUGH THERMAL SPRAYING TESTING
,
p. 4356-4367.
In: 65º Congresso ABM,
Rio de Janeiro,
2010.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-16889