MICRODUREZA DAS FASES EM AÇOS FEALNBC TEMPERADOS EM ÁGUA E ÓLEO: MICROHARDNESS OF PHASES IN FEALNBC STEELS QUENCHED IN WATER AND OIL

AçOS LEVES LIGADOS AO ALUMíNIO TêM GANHADO NOTORIEDADE DEVIDO A COMBINAçãO DE BAIXA DENSIDADE E ELEVADA RESISTêNCIA MECâNICA. O PROCESSAMENTO DESTES AçOS ENVOLVE PRINCIPALMENTE LAMINAçõES A QUENTE E RESFRIAMENTO CONTROLADO. O DESENVOLVIMENTO RECENTE DESSES AçOS GERA A NECESSIDADE DE MAIS ESTUDOS SOBRE MICROESTRUTURA EM DIFERENTES CONDIçõES DE RESFRIAMENTO. ESTE TRABALHO VISA AVALIAR A MICROESTRUTURA DE DUAS LIGAS DE AçO FEALNBC SUBMETIDAS A NORMALIZAçãO, TEMPERA EM ÁGUA E TEMPERA EM ÓLEO. A CARACTERIZAçãO DAS FASES PRESENTES DE ACORDO COM CADA TRATAMENTO TéRMICO FOI REALIZADA ATRAVéS DE IMAGENS DE MICROSCOPIA ELETRôNICA DE VARREDURA E MICRODUREZA VICKERS. A AMOSTRA NORMALIZADA APRESENTA MATRIZ DE FERRITA δ, E AUSTENITA RETIDA E LAMELAS DE FERRITA α COM CARBONETO κ, Já AS AMOSTRAS TEMPERADAS APRESENTARAM MARTENSITA, A LIGA COM MENOR TEOR DE ALUMíNIO APRESENTOU MAIORES DUREZAS EM TODAS AS CONDIçõES E A TEMPERA EM áGUA PROMOVEU O MAIOR ENDURECIMENTO DAS FASES.

ALUMINUM-ALLOYED LIGHTWEIGHT STEELS HAVE GAINED NOTORIETY DUE TO THEIR COMBINATION OF LOW DENSITY AND HIGH MECHANICAL STRENGTH. THE PROCESSING OF THESE STEELS MAINLY INVOLVES HOT ROLLING AND CONTROLLED COOLING. THE RECENT DEVELOPMENT OF THESE STEELS GENERATES THE NEED FOR FURTHER STUDIES ON MICROSTRUCTURE UNDER DIFFERENT COOLING CONDITIONS. THIS WORK AIMS TO EVALUATE THE MICROSTRUCTURE OF TWO FEALNBC STEEL ALLOYS SUBJECTED TO NORMALIZATION, WATER QUENCHING, AND OIL QUENCHING. THE CHARACTERIZATION OF THE PHASES PRESENT ACCORDING TO EACH HEAT TREATMENT WAS PERFORMED THROUGH SCANNING ELECTRON MICROSCOPY AND VICKERS MICROHARDNESS IMAGES. THE NORMALIZED SAMPLE PRESENTS A δ-FERRITE MATRIX, RETAINED AUSTENITE, AND α-FERRITE LAMELLAE WITH κ-CARBIDE, WHILE THE QUENCHED SAMPLES PRESENTED MARTENSITE. THE ALLOY WITH THE LOWEST ALUMINUM CONTENT PRESENTED HIGHER HARDNESS IN ALL CONDITIONS AND WATER QUENCHING PROMOTED THE GREATEST HARDENING OF THE PHASES.

Palavras-chave

Aços Leves, FeAlNbC, MEV, Normalização, Têmpera

Lightweight Steel, FeAlNbC, SEM, Tempering, Quenching

Como citar

JR, EUSTAQUIO DE SOUZA BAETA; AGUILERA, LETÍCIA DOS SANTOS; CAMPOS, JOSÉ BRANT DE; PERIPOLLI, SUZANA BOTTEGA; SANTOS, KELLEN VENÂNCIO DOS; SILVA, CAMILA ALVES PELICARTO DA; CASTRO, AMANDA ALMEIDA DE. MICRODUREZA DAS FASES EM AÇOS FEALNBC TEMPERADOS EM ÁGUA E ÓLEO , p. 3214-3220. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-41381