MICROESTRUTURA, DENSIDADE E POROSIDADE DE HIDROXIAPATITA CONFORMADA POR ICE-TEMPLATING: MICROSTRUCTURE, DENSITY AND POROSITY OF HYDROXYAPATITE CONFORMED BY ICE-TEMPLATING

A HIDROXIAPATITA é UMA CERâMICA MULTIFUNCIONAL QUE PODE SER UTILIZADA EM IMPLANTES DEVIDO A BOA BIOCOMPATIBILIDADE, OSTEOCONDUçãO E BIOATIVIDADE, ALéM DE NãO SER TóXICA E PERMITIR A FáCIL SUBSTITUIçãO DE CáTIONS E âNIONS. ELA TAMBéM TEM ALTA RELEVâNCIA NA áREA AMBIENTAL, SENDO UTILIZADA EM CATALISADORES E FILTROS. EM AMBOS OS CASOS SãO BUSCADAS ESTRUTURAS POROSAS E MéTODOS DE PRODUçãO DESSAS ESTRUTURAS ESTãO EM CONSTANTE DESENVOLVIMENTO. ESTE TRABALHO VISA COMPARAR A UTILIZAçãO DE PEG-4000 E PEG-6000 COMO LIGANTE EM CONCENTRAçãO DE 4% EM PESO. PARA MELHORAR O COMPORTAMENTO REOLóGICO, O PH DA áGUA FOI AJUSTADO PARA 11,8 UTILIZANDO NAOH. AS AMOSTRAS FORAM CONGELADAS, LIOFILIZADAS E SINTERIZADAS A 1150 °C POR 6 HORAS. A MORFOLOGIA DOS POROS FOI CARACTERIZADA POR MEIO DE ANáLISES DE MICROSCOPIA ELETRôNICA DE VARREDURA (MEV) E A POROSIDADE APARENTE PELO MéTODO DE ARQUIMEDES. O PEG-4000 APRESENTOU MAIOR HOMOGENEIDADE NO TAMANHO DE POROS ENQUANTO O PEG-6000 APRESENTOU ESTRUTURA MAIS PRONUNCIADA E BEM DEFINIDA. A POROSIDADE APARENTE ENCONTRADA PARA O PEG-4000 FOI DE 51,03% E PARA O PEG-6000, 49,11%.

HYDROXYAPATITE IS A MULTIFUNCTIONAL CERAMIC THAT CAN BE USED IN IMPLANTS DUE TO ITS GOOD BIOCOMPATIBILITY, OSTEOCONDUCTION AND BIOACTIVITY, IN ADDITION TO BEING NON-TOXIC AND ALLOWING EASY REPLACEMENT OF CATIONS AND ANIONS. IT ALSO HAS HIGH RELEVANCE IN THE ENVIRONMENTAL AREA, BEING USED IN CATALYSTS AND FILTERS. IN BOTH CASES, POROUS STRUCTURES ARE SOUGHT AND METHODS OF PRODUCING THESE STRUCTURES ARE CONSTANTLY DEVELOPING. THIS WORK AIMS TO COMPARE THE USE OF PEG-4000 AND PEG-6000 AS A LIGAND AT A CONCENTRATION OF 4%WT. TO IMPROVE THE RHEOLOGICAL BEHAVIOR, THE PH OF THE WATER WAS ADJUSTED TO 11.8 USING NAOH. THE SAMPLES WERE FROZEN, FREEZE-DRIED AND SINTERED AT 1150 °C FOR 6 HOURS. THE MORPHOLOGY OF THE PORES WAS CHARACTERIZED USING SCANNING ELECTRON MICROSCOPY (SEM) ANALYZES AND THE APPARENT POROSITY USING THE ARCHIMEDES METHOD. PEG-4000 PRESENTED GREATER HOMOGENEITY IN PORE SIZE WHILE PEG-6000 PRESENTED A MORE PRONOUNCED AND WELL-DEFINED STRUCTURE. THE APPARENT POROSITY FOUND FOR PEG-4000 WAS 51.03% AND FOR PEG-6000, 49.11%.

Palavras-chave

Hidroxiapatita; Estruturas porosas; Ice-templating; Processamento de materiais cerâmicos

Hydroxyapatite; Porous scaffolds; Ice templating; Ceramic materials processing.

Como citar

BOTÃO, CAMILA ALVES PELICARTO DA SILVA; SANTOS, KELLEN VENANCIO DOS; JÚNIOR, EUSTÁQUIO DE SOUZA BAÊTA; AGUILERA, LETÍCIA DOS SANTOS; PERIPOLLI, SUZANA BOTTEGA; CAMPOS, JOSÉ BRANT DE. MICROESTRUTURA, DENSIDADE E POROSIDADE DE HIDROXIAPATITA CONFORMADA POR ICE-TEMPLATING , p. 1373-1381. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.