MICROESTRUTURA E PROPRIEDADES MAGNÉTICAS DA FERRITA Ni-Zn DOPADA COM SAMÁRIO

MICROSTRUCTURE AND MAGNETIC PROPERTIES OF NI-ZN FERRITE DOPED WITH SAMARIUM

DOI

10.5151/1516-392X-24845

Downloads

Baixar Artigo 336 Downloads

Resumo

Ferritas são compostos cerâmicos que apresentam propriedades magnéticas, sendo estas dependentes da sua estrutura cristalina. Dentre as ferritas, a do tipo Ni-Zn é uma das mais promissoras, em virtude da microestrutura e das propriedades magnéticas deste material. Este trabalho teve como objetivo analisar a microestrutura e propriedades magnéticas da ferrita Ni-Zn dopada com íons (TR) Sm3+. A ferrita Ni-Zn-Sm foi obtida pelo método dos precursores poliméricos, a partir da dissolução do ácido cítrico, nitrato de ferro, nitrato de níquel, nitrato de zinco, nitrato de samário e etilenoglicol. A resina obtida foi pirolisada a 350°C/2h com taxa de aquecimento de 10°C/min. e calcinada a 650°C/3h com taxa de aquecimento de 10°C/min. O material resultante foi caracterizado por difração de raios-X (DRX), microscopia eletrônica de varredura (MEV) e magnetometria de amostra vibrante (VSM). Os resultados mostraram a formação de fase única da ferrita Ni-Zn-Sm, com partículas aglomeradas e características magnéticas de material macio "soft", com baixa coercividade (0,189 kOe) e magnetização de saturação (47,699 emu/g).

 

Ferrites are ceramic compounds which exhibit magnetic properties, which are dependent on its crystal structure. Among ferrites, the Ni-Zn type is one of the most promising, due to the microstructure and the magnetic properties of this material. This work aimed to analyze the microstructure and magnetic properties of Ni-Zn ferrite doped with ions (TR) Sm3+. The Sm-Ni-Zn ferrite was obtained by polymeric precursors by dissolving citric acid, iron nitrate, nickel nitrate, zinc nitrate, samarium nitrate and ethylene glycol. The obtained resin was pyrolyzed at 350°C/2h with a heating rate of 10°C/ min. and calcined at 650°C/3h with a heating rate of 10°C/ min. The resulting material was characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and vibrating sample magnetometry (VSM). The results showed the formation of single phase Ni-Zn ferrite, Sm, and agglomerated particles with magnetic properties of soft material "soft", low coercivity (0,189 kOe) and saturation magnetization (47,699 emu/ g).

Palavras-chave

Ferrita; Ni-Zn-Sm; Propriedades magnéticas; Samário

Ferrite; Ni-Zn-Sm; Magnetic properties; Samarium

Como citar

Raimison Bezerra de Assis; Flanelson Maciel Monteiro; Samara Melo Valcacer; Ariadne de Souza Silva; Maurício Roberto Bomio Delmonte; Carlos Alberto Paskocimas; Rubens Maribondo do Nascimento; Uílame Umbelino Gomes; Fabiana Villela da Motta. MICROESTRUTURA E PROPRIEDADES MAGNÉTICAS DA FERRITA Ni-Zn DOPADA COM SAMÁRIO , p. 8159-8164. In: 69° Congresso Anual da ABM - Internacional, São Paulo - Brasil, 2014.