NOVA TECNOLOGIA PARA CONTROLE DE CORROSÃO EM SISTEMAS ABERTOS DE MOLDE

NEW TECHNOLOGY FOR CORROSION CONTROL IN OPEN MOLD SYSTEMS

Autoria

Amorim, Caroline Morgado

Amorim, Caroline Morgado

4 Artigos, Baixados 30 Vezes

DOI

10.5151/2594-5300-34841

Downloads

Resumo

SISTEMAS ABERTOS DE RESFRIAMENTO DE MOLDES TêM-SE CONSTITUíDO UM GRANDE DESAFIO PARA O CONDICIONAMENTO QUíMICO. O USO DOS PROGRAMAS TRADICIONAIS GERAM UM POTENCIAL ELEVADO DE DEPOSIçãO DEVIDO à ELEVADA TAXA DE TROCA TéRMICA E àS CARACTERíSTICAS DA áGUA DE RECIRCULAçãO. PARA FAZER FRENTE A ESTES RISCOS, UMA SIDERúRGICA BRASILEIRA NãO UTILIZAVA INIBIDOR DE CORROSãO PARA AçO CARBONO PARA REDUZIR A PROBABILIDADE DE DEPOSIçãO NOS MOLDES. COMO CONSEQUêNCIA AS TAXAS DE CORROSãO EM AçO CARBONO ERAM ELEVADAS, A VIDA úTIL DOS MOLDES E A PRODUTIVIDADE DA UNIDADE ERA SEVERAMENTE COMPROMETIDA. A NALCO WATER DESENVOLVEU UMA NOVA TECNOLOGIA DENOMINADA PEARL QUE ATUA COMO INIBIDOR DE CORROSãO PARA AçO CARBONO SEM AUMENTAR O POTENCIAL INCRUSTANTE DO SISTEMA. ESSA TECNOLOGIA FOI IMPLEMENTADA NESTA SIDERúRGICA E APENAS NO PRIMEIRO MêS DE APLICAçãO FOI POSSíVEL: REDUZIR 55% NA TAXA DE CORROSãO DE AçO CARBONO, ENQUADRANDO O PARâMETRO NA ESPECIFICAçãO TéCNICA O QUE LEVOU AO AUMENTO DA CONFIABILIDADE OPERACIONAL PELO AUMENTO DO DESEMPENHO DO SISTEMA DE RESFRIAMENTO DOS MOLDES. HOUVE UMA REDUçãO DE 91% NA TAXA DE PRODUTOS NãO CONFORMES POR TRINCAS, COM UM IMPACTO ANUAL DE USD 350K.

OPEN MOLD COOLING SYSTEMS HAVE BEEN A MAJOR CHALLENGE FOR CHEMICAL CONDITIONING. THE USE OF TRADITIONAL PROGRAMS GENERATES A HIGH POTENTIAL FOR DEPOSITION DUE TO THE HIGH RATE OF HEAT EXCHANGE AND THE CHARACTERISTICS OF THE RECIRCULATING WATER. TO FACE THESE RISKS, A BRAZILIAN STEELMAKER DID NOT USE A CORROSION INHIBITOR FOR CARBON STEEL TO REDUCE THE LIKELIHOOD OF DEPOSITION IN THE MOLDS. AS A RESULT, CORROSION RATES ON CARBON STEEL WERE HIGH, AND MOLD LIFE AND FACILITY PRODUCTIVITY WERE SEVERELY COMPROMISED. NALCO WATER HAS DEVELOPED A NEW TECHNOLOGY CALLED PEARL THAT ACTS AS A CORROSION INHIBITOR FOR CARBON STEEL WITHOUT INCREASING THE FOULING POTENTIAL OF THE SYSTEM. THIS TECHNOLOGY WAS IMPLEMENTED IN THIS STEEL MILL AND IN THE FIRST MONTH OF APPLICATION ALONE IT WAS POSSIBLE TO REDUCE THE CORROSION RATE OF CARBON STEEL BY 55%, FITTING THE PARAMETER INTO THE TECHNICAL SPECIFICATION, WHICH LED TO AN INCREASE IN OPERATIONAL RELIABILITY BY INCREASING THE PERFORMANCE OF THE COOLING SYSTEM OF THE MOLDS. THERE WAS A 91% REDUCTION IN THE RATE OF NON-CONFORMING PRODUCTS DUE TO CRACKS, WITH AN ANNUAL IMPACT OF OVER USD 350K.

Palavras-chave

Molde; Sistema Aberto; Corrosão; Pearl

Mold; Cooling Systems; Corrosion; Pearl