NOVAS FORMULAÇÕES SOL-GEL PARA AUMENTAR O EFEITO BARREIRA NA PROTEÇÃO CONTRA A CORROSÃO DO AÇO GALVANIZADO

NEW SOL-GEL FORMULATIONS TO INCREASE THE BARRIER EFFECT OF A PROTECTIVE COATING AGAINST THE CORROSION OF GALVANIZED STEEL

DOI

10.5151/2594-4711-22946

Downloads

Baixar Artigo 245 Downloads

Resumo

O zinco apresenta taxas de corrosão inferiores ao aço em atmosferas naturais. Assim, sua adequação como revestimento protetor do aço é devida a dois fatores: proteção catódica oferecida ao aço nas descontinuidades do revestimento e taxas de corrosão baixas permitindo longos períodos de proteção. Neste sentido, tem sido desenvolvido uma nova formulação com a introdução de um agente plastificante com o objetivo de aumentar a espessura de camada para revestir de forma uniforme e homogenea o aço galvanizado que possui uma rugosidade bastante heterogênea. O objetivo do trabalho é revestir o aço galvanizado com um filme híbrido obtido a partir de um sol constituído pelos precursores alcoóxidos: 3-(trimetoxisililpropil)metacrilato (TMSM) e tetraetoxisilano (TEOS) com adição de nitrato de cério na concentração de 0,01M. Avaliou-se a influência da concentração (20, 40, 60 e 80 g/L) de plastificante de polietileno glicol na formulação do sol. Os filmes foram obtidos pelo processo de dip-coating. Os filmes híbridos obtidos foram caracterizados quanto ao comportamento eletroquímico e morfológico. Resultados mostraram que os filmes híbridos obtidos com concentrações de plastificante (20, 40 e 60 g/L) apresentaram maiores de espessura de camada e conseqüentemente melhor desempenho eletroquímico.

 

Zinc has lower corrosion rates compared to steel in natural atmospheres. Thus, its adequacy as a protective coating steel is due to two factors: cathodic protection afforded to steel discontinuities in the coating and corrosion rates low allowing longer periods of protection. A new formulation has been developed with the introduction of a plasticizer in order to increase the thickness of layer to coat evenly and homogeneously the galvanized steel which has a very heterogeneous roughness. The objective is to coat galvanized steel with a hybrid film obtained from a sol constituted by the alkoxide precursors: 3 - (trimethoxysilylpropyl) methacrylate (TMSM), with tetraethoxysilane (TEOS) with addition of nitrate cerium in a concentration of 0.01 M. It was evaluated the influence of the concentration (20, 40, 60 and 80 g / L) of polyethylene glycol plasticizer in the formulation of the sol. The films were obtained by dip-coating process. The hybrid films were characterized as the morphological and electrochemical behavior. Results showed that the hybrid films obtained with concentrations of plasticizer (20, 40 and 60 g/L) presented higher layer thickness and consequently better electrochemical performance.

Palavras-chave

Filme híbrido; PEG; Corrosão; Aço galvanizado

Hybrid film; PEG; Corrosion; Galvanized steel.

Como citar

Kunst, Sandra Raquel; Parise, Karine; Bertoli, Paloma; Ludwig, Gustavo; Malfatti, Célia de Fraga. NOVAS FORMULAÇÕES SOL-GEL PARA AUMENTAR O EFEITO BARREIRA NA PROTEÇÃO CONTRA A CORROSÃO DO AÇO GALVANIZADO , p. 83-93. In: 13º ENEMET - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas, São Paulo - Brasil, 2013.