O IMPACTO DA INCORPORAÇÃO DE RESÍDUOS DE UVA NAS PROPRIEDADES TECNOLÓGICAS DA CERÂMICA VERMELHA

THE IMPACT OF INCORPORATING GRAPE WASTE INTO THE TECHNOLOGICAL PROPERTIES OF RED CERAMIC

Autoria

MENDES, RENATA RIBEIRO; FERREIRA, ELVIS PANTALEÃO; DELAQUA, GEOVANA CARLA GIRONDI; VIEIRA, CARLOS MAURÍCIO FONTES; AZEVEDO, AFONSO RANGEL GARCEZ DE

MENDES, RENATA RIBEIRO

Eu sou esse autor

FERREIRA, ELVIS PANTALEÃO

Eu sou esse autor

DELAQUA, GEOVANA CARLA GIRONDI

Eu sou esse autor

VIEIRA, CARLOS MAURÍCIO FONTES

Eu sou esse autor

AZEVEDO, AFONSO RANGEL GARCEZ DE

Eu sou esse autor

DOI

10.5151/2594-5327-41288

Downloads

Resumo

O OBJETIVO DESTE TRABALHO FOI ESTUDAR OS EFEITOS DA INTRODUçãO DE RESíDUOS DE UVA NAS CARACTERíSTICAS TECNOLóGICAS DAS CERâMICAS APóS O PROCESSO DE QUEIMA. A ANáLISE DE COMPOSIçãO FOI CONDUZIDA ATRAVéS DA FLUORESCêNCIA DE RAIOS-X (FRX), SEGUIDA PELO PROCESSAMENTO DAS MATéRIAS-PRIMAS PARA GARANTIR PARTíCULAS DE TAMANHO UNIFORME. FORMULAçõES FORAM ELABORADAS, INCORPORANDO ATé 5% DE RESíDUOS DE UVA, SENDO ENTãO UMEDECIDAS E MOLDADAS EM CORPOS DE PROVA. APóS A QUEIMA EM DIFERENTES TEMPERATURAS, PROPRIEDADES COMO ABSORçãO DE áGUA, RETRAçãO LINEAR, RESISTêNCIA à FLEXãO E íNDICE DE PLASTICIDADE FORAM METICULOSAMENTE AVALIADAS. OS RESULTADOS REVELARAM UM AUMENTO NA RETRAçãO LINEAR E ABSORçãO DE áGUA CONFORME A QUANTIDADE DE RESíDUOS DE UVA AUMENTAVA, ENQUANTO A RESISTêNCIA à FLEXãO APRESENTOU UMA TENDêNCIA DE REDUçãO. CONCLUIU-SE QUE A ADIçãO DE RESíDUOS DEVE SER REALIZADA COM CAUTELA PARA PRESERVAR A QUALIDADE FINAL DA CERâMICA. ESTE ESTUDO PROPORCIONA PERSPECTIVAS VALIOSAS PARA O AVANçO SUSTENTáVEL DA INDúSTRIA CERâMICA, AO EXPLORAR O POTENCIAL DOS RESíDUOS DE UVA COMO MATéRIA-PRIMA.

THE AIM OF THIS WORK WAS TO STUDY THE EFFECTS OF INTRODUCING GRAPE WASTE ON THE TECHNOLOGICAL CHARACTERISTICS OF CERAMICS AFTER THE FIRING PROCESS. COMPOSITIONAL ANALYSIS WAS CARRIED OUT USING X-RAY FLUORESCENCE (XRF), FOLLOWED BY PROCESSING OF THE RAW MATERIALS TO ENSURE UNIFORM PARTICLE SIZE. VARIOUS FORMULATIONS WERE PREPARED, INCORPORATING UP TO 5% GRAPE WASTE, WHICH WAS THEN MOISTENED AND MOLDED INTO TEST SPECIMENS. AFTER FIRING AT DIFFERENT TEMPERATURES, PROPERTIES SUCH AS WATER ABSORPTION, LINEAR SHRINKAGE, FLEXURAL STRENGTH AND PLASTICITY INDEX WERE METICULOUSLY EVALUATED. THE RESULTS REVEALED AN INCREASE IN LINEAR SHRINKAGE AND WATER ABSORPTION AS THE AMOUNT OF GRAPE WASTE INCREASED, WHILE FLEXURAL STRENGTH SHOWED A DOWNWARD TREND. IT WAS CONCLUDED THAT THE ADDITION OF WASTE SHOULD BE CARRIED OUT WITH CAUTION IN ORDER TO PRESERVE THE FINAL QUALITY OF THE CERAMIC. THIS STUDY PROVIDES VALUABLE PERSPECTIVES FOR THE SUSTAINABLE ADVANCEMENT OF THE CERAMICS INDUSTRY BY EXPLORING THE POTENTIAL OF GRAPE WASTE AS A RAW MATERIAL.

Palavras-chave

Cerâmica vermelha; vinícola; resíduo; Incorporação.

Red ceramics; winery; waste; incorporation.