O PAPEL DO NIóBIO EM AçOS DE BAIXA LIGA TEMPERADOS E REVENIDOS: UMA REVISãO

NIOBIUM ROLE IN QUENCHED AND TEMPERED LOW ALLOY STEELS: A REVIEW

Autoria

GORNI, ANTONIO AUGUSTO

GORNI, ANTONIO AUGUSTO

Eu sou esse autor

DOI

10.5151/2594-5297-41026

Downloads

Resumo

NAS ÚLTIMAS DÉCADAS FORAM PUBLICADOS INÚMEROS TRABALHOS SOBRE A INFLUÊNCIA DO NIÓBIO NA LAMINAÇÃO TERMOMECÂNICA DE AÇOS ESTRUTURAIS DE BAIXO CARBONO. POR OUTRO LADO, SEU PAPEL EM AÇOS TEMPERADOS REVENIDOS FOI MUITO MENOS INVESTIGADO E DISCUTIDO, PROVAVELMENTE DEVIDO AO EFEITO LIMITADO DO NIÓBIO NA TEMPERABILIDADE DA AUSTENITA DEVIDO ÀS ALTAS TEMPERATURAS REQUERIDAS PARA SUA TOTAL DISSOLUÇÃO, O QUE LIMITA SUA AMPLA ADOÇÃO NESTA APLICAçãO. A EVOLUçãO DAS TéCNICAS DE MICROSCOPIA ELETRôNICA, ESPECIALMENTE MET E EBSD, LANçARAM MAIS LUZ SOBRE O EFEITO DO NIóBIO NA MORFOLOGIA MICORESTRUTURAL DA MARTENSITA TEMPERADA E REVENIDA. ESTE TRABALHO TEM COMO OBJETIVO FAZER UMA REVISãO SOBRE O PAPEL DO NIóBIO NA METALURGIA DA TêMPERA E REVENIDO, PARA PROMOVER SEU USO EM PROJETOS DE LIGA MAIS EFICIENTES TANTO DO PONTO DE VISTA DA SUSTENTABILIDADE COMO DE CUSTO. PARA CITAR UM EXEMPLO, A ADIçãO DE 0,060% NB A UM AçO USADO NA MANUFATURA DE TUBOS OCTG TEMPERADOS E REVENIDOS AUMENTOU O SEU LIMITE DE ESCOAMENTO DE 719 MPA PARA 796 DEVIDO àS CONTRIBUIçõES ADICIONAIS DE ENDURECIMENTO DECORRENTES DO REFINO DA MARTENSITA, DENSIDADE DE DISCORDANCIAS E PRECIPITAçãO.

IN RECENT DECADES COUNTLESS WORKS HAVE BEEN PUBLISHED ON THE INFLUENCE OF NIOBIUM IN THE THERMOMECHANICAL ROLLING OF STRUCTURAL LOW CARBON STEELS. ON THE OTHER HAND, ITS ROLE IN QUENCHED AND TEMPERED STEELS HAS BEEN MUCH LESS INVESTIGATED AND DISCUSSED, PERHAPS DUE TO THE LIMITED EFFECT OF NIOBIUM ON AUSTENITE HARDENABILITY DUE TO THE HIGH TEMPERATURES REQUIRED FOR ITS FULL DISSOLUTION THAT PREVENTS ITS WIDE ADOPTION FOR THIS APPLICATION. THE EVOLUTION OF ELECTRON MICROSCOPY TECHNIQUES, PARTICULARLY MET AND EBSD, HAS SHED MORE LIGHT ABOUT THE EFFECT OF NIOBIUM ON THE MICROSTRUCTURAL MORPHOLOGY OF QUENCHED AND TEMPERED MARTENSITE. THIS WORK AIMS TO REVIEW THE ROLE OF NIOBIUM IN QUENCHING AND TEMPERING METALLURGY OF LOW ALLOY STEELS, IN ORDER TO PROMOTE ITS USE IN MORE EFFICIENT ALLOY DESIGNS FROM AN ENVIRONMENTAL AND COST POINT OF VIEW. AS AN EXAMPLE, THE ADDITION OF 0.060% NB TO A STEEL USED FOR THE MANUFACTURE OF OCTG QUENCHED AND TEMPERED PIPES INCREASED YIELD STRENGTH FROM 719 MPA TO 796 MPA DUE TO THE ADDITIONAL HARDENING CONTRIBUTIONS OF MARTENSITE REFINING, DISLOCATION DENSITY AND PRECIPITATION.

Palavras-chave

nióbio; têmpera e revenido; martensita; precipitação

Niobium; Quenching and Tempering; Martensite; Precipitation.