NO PRESENTE TRABALHO O OBJETIVO FOI AVALIAR A VIABILIDADE DE DESENVOLVER UMA CERÂMICA DE REVESTIMENTO UTILIZANDO COMO MATERIAL UMA MASSA CERÂMICA ARGILOSA COM INCORPORAÇÃO DE RESÍDUO DE VIDRO PLANO. DUAS MASSAS FORAM FORMULADAS, UMA MASSA ARGILOSA COM 0% DE RESÍDUO, QUE SERVIU DE REFERÊNCIA, E OUTRA COM 20% DE RESÍDUO DE VIDRO PLANO. CORPOS DE PROVA FORAM PREPARADOS POR PRENSAGEM UNIAXIAL 12,5 MPA E POSTERIORMENTE SUBMETIDOS AO PROCESSO DE QUEIMA EM TEMPERATURAS DE 1000, 1050, 1100, 1150 E 1200°C. AS MATÉRIAS-PRIMAS FORAM SUBMETIDAS À CARACTERIZAÇÃO QUÍMICA, MINERALÓGICA E TÉRMICA. FORAM AVALIADAS AS PROPRIEDADES FÍSICAS E MECÂNICAS COMO, RETRAÇÃO LINEAR, ABSORÇÃO DE ÁGUA, POROSIDADE APARENTE E RESISTÊNCIA MECÂNICA À FLEXÃO DOS CORPOS DE PROVA QUEIMADOS. O REAPROVEITAMENTO DO RESÍDUO DE VIDRO PLANO NA INDÚSTRIA CERÂMICA PODE FAVORECER A REDUÇÃO DA TEMPERATURA DE SINTERIZAÇÃO, GERANDO PRODUTOS DE MELHOR QUALIDADE. COM BASE NOS RESULTADOS OBTIDOS NESSA PESQUISA, VERIFICOU-SE QUE O RESÍDUO ADICIONADO EM 20% POSSIBILITOU AMOSTRAS QUE ATENDERAM AS ESPECIFICAÇÕES DE FABRICAÇÃO DE REVESTIMENTO POROSO (AZULEJO), TORNANDO POSSÍVEL SEU REAPROVEITAMENTO NA INDÚSTRIA DE CERÂMICA VERMELHA.
IN THE PRESENT WORK, THE OBJECTIVE WAS TO EVALUATE THE FEASIBILITY OF DEVELOPING A VENEERING CERAMIC USING AS MATERIAL A CLAYEY CERAMIC MASS WITH INCORPORATION OF FLAT GLASS RESIDUE. TWO MASSES WERE FORMULATED, ONE WITH ONLY CLAY MASS, WITH 0% RESIDUE AND THE OTHER WITH 20% FLAT GLASS RESIDUE. SPECIMENS WERE PREPARED BY UNIAXIAL PRESSING AT 12.5 MPA AND SUBSEQUENTLY SUBMITTED TO THE FIRING PROCESS AT TEMPERATURES OF 1000, 1050, 1100, 1150 AND 1200°C. THE RAW MATERIALS WERE SUBJECTED TO CHEMICAL, MINERALOGICAL AND THERMAL CHARACTERIZATION. THE PHYSICAL AND MECHANICAL PROPERTIES SUCH AS LINEAR SHRINKAGE, WATER ABSORPTION, APPARENT POROSITY AND MECHANICAL RESISTANCE TO BENDING OF THE BURNED SPECIMENS WERE EVALUATED. THE REUSE OF FLAT GLASS WASTE IN THE CERAMIC INDUSTRY CAN FAVOR THE REDUCTION OF THE SINTERING TEMPERATURE, GENERATING BETTER QUALITY PRODUCTS. BASED ON THE RESULTS OBTAINED IN THIS RESEARCH, IT WAS FOUND THAT THE RESIDUE ADDED IN 20% ALLOWED SAMPLES THAT MET THE SPECIFICATIONS FOR MANUFACTURING POROUS COATING (TILE), MAKING IT POSSIBLE TO REUSE IT IN THE RED CERAMIC INDUSTRY
Palavras-chave
Cerâmica vermelha; Resíduo de vidro plano; Revestimento poroso
Red ceramic; Flat glass waste; Porous coating
Como citar
Delaqua, Geovana Carla Girondi;
Riscado, Ana Laura Lopes de Matos;
Pires, Diego Alexsander Moreira;
Souz, Djalma;
Jr, Fernando Vernilli;
Vieira, Carlos Maurício Fontes.
OBTENÇÃO DE CERÂMICA DE REVESTIMENTO COM RESÍDUO DE VIDRO PLANO
,
p. 3089-3099.
In: 75° Congresso Anual da ABM,
São Paulo,
2022.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-34934