Título

OBTENÇÃO E CARACTERIZAÇÃO DE COMPÓSITOS NANOESTRUTURADOS SUPERABRASIVOS VIA SINTERIZAÇÃO EM ALTAS PRESSÕES E ALTAS TEMPERATURAS NO SISTEMA cBN-TiB2-Al

OBTAINING AND CHARACTERIZATION OF NANOSTRUCTURED SUPERABRASIVE COMPOSITES THROUGH SINTERING IN HIGH PRESSURES AND HIHG TEMPERATURES IN THE SYSTEM cBN-TiB2-Al

DOI

10.5151/2594-5327-21381

Downloads

Baixar Artigo 121 Downloads

Resumo

O cBN é um material promissor dentre esses materiais. Neste contexto, no presente trabalho são apresentados resultados referentes ao desenvolvimento e caracterização de compósitos nanoestruturados. O alumínio e o diboreto de titânio foram utilizados como ligantes no processo de sinterização do cBN. Inicialmente os pós de cBN e ligantes foram misturados em moinho de alta energia do tipo SPEX visando a cominuição dos mesmos até a forma de nanopó. O tamanho médio de partícula encontrado após a moagem variou entre 200 nm a 500 nm. O aperfeiçoamento das técnicas de usinagem assim como o desenvolvimento da indústria metal/mecânica, tem sido relacionado principalmente a aplicações de novos materiais avançados e a ferramentas de corte para materiais ferrosos. Após o processo de mistura os pós foram compactados e submetidos ao processo de sinterização. Os compósitos obtidos foram caracterizados em termo de microestrutura, propriedades mecânicas. Foram ainda realizados ensaios de torneamento em aço endurecido. Os resultados mostraram que os compósitos obtidos são apropriados para fabricação de insertos destinados para usinagem de alta velocidade e materiais tais como ferro nodular.

 

The cBN is a promising material among these materials. In this context, this work presents results for the development and characterization of nanostructured composites. Aluminum and titanium diboride as binders were used in the process of cBN. Initially, the cBN powder and binder were mixed in a high energy mill SPEX order to comminution thereof to from nanopower. The average particle size after milling found ranged between 200 nm to 500 nm. The improvement of machining techniques and the development of industry metal/mechanics has been primarily related to applications of new advanced materials and cutting tools for ferrous materials. After the mixing the powers were compacted and subjected to sintering process. The composites were characterized in terms of microstructure and mechanical properties. Were even conducted tests on hardened steel turning the results show that the composites are suitable for manufacturing inserts designed for high speed machining of materials such as ductile iron.

Palavras-chave

cBN, Sinterização, Usinagem, sistema cBN-TiB2-Al.

cBN, Sintering, Machining, system cBN-TiB2-Al.

Como citar

Silva, Samara Venina Simen de Azeredo; Skury, Ana Lúcia Diegues; Azevedo, Márcia Giardinieri de; Monteiro, Sérgio Neves. OBTENÇÃO E CARACTERIZAÇÃO DE COMPÓSITOS NANOESTRUTURADOS SUPERABRASIVOS VIA SINTERIZAÇÃO EM ALTAS PRESSÕES E ALTAS TEMPERATURAS NO SISTEMA cBN-TiB2-Al , p. 2990-2998. In: 67º Congresso da ABM - Internacional / 12º ENEMET - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas, Rio de Jabeiro, 2012.