OS TIPOS DE CORROSÃO EM UM PRÉDIO TIPO P2

THE CORROSION TYPES IN A P2 BUILDING

DOI

10.5151/1516-392X-32063

Downloads

Baixar Artigo 214 Downloads

Resumo

Este trabalho apresenta as patologias desencadeadas em um prédio tipo P2 localizado em Dresden, na Alemanha. Esses danos são resultado da metodologia utilizada durante o processo de reconstrução da parte oriental do país, dividido na Guerra Fria, logo após a Segunda Guerra Mundial, e as condições ambientais a que o prédio estava submetido. O objetivo deste trabalho é investigar as causas tecnológicas, geográficas, econômicas e históricas que levaram à degradação relativamente precoce das moradias da República Democrática Alemã. Foi feita uma análise visual e fotográfica das patologias macroscópicas presentes no edifício Gret-Palucca-9, em Dresden e assim elaboradas as caracterizações dos danos e metodologias de recuperação e manutenção. A maior parte das patologias causadas são os diferentes tipos de corrosão, tanto da armadura quanto do concreto, consequentes das normas de construção vigentes e das condições climáticas da cidade. A partir do resultado encontrado, é possível entender que a durabilidade e vida útil de prédios pode ser menorizada quando elementos como a pressa na execução da obra, a qualidade dos materiais, a falta de normas e metodologia eficientes são subvalorizados.

 

This work presents the pathologies evolution in a P2 building located in Dresden, Germany. These damages are a result of the methodology used during the rebuilding process from the east part of the country, divided at the Cold War, just after the Second World War, and the envirommental conditions that the building was exposed. The work’s main goal is dig the fundamental reasons as technology, geographic, economic and historical causes wich brought the relatively early degradation from the German Democratic Republic buildings. It was done a visual and photographic evaluation of the macroscopic pathologies in the Gret-Palucca-9 building, in Dresden, then the damage description was made and a methodoly of repair and preventive maintenance formulated. The major pathologies are different kinds of corrosion from the steel and also the concrete, they are consenquences of the current construction rules and the city wetter. From the found result, it is possible to understand that the buidings life time and durability can be shorter when the execution rush, materials selection, absence of rules and right methodologies are underestimated.

Palavras-chave

Corrosão; Patologia; Construção; Recuperação

Corrosion; Pathology; Construction; Repair