A LIMPIDEZ DO AÇO SE TORNOU EXTREMAMENTE IMPORTANTE AO LONGO DOS ANOS, O QUE FEZ COM QUE ACIARISTAS DEDICASSEM AO ESTUDO DE PARÂMETROS DE PROCESSO QUE POSSIBILITAM A OTIMIZAÇÃO DO PROCESSO VIZANDO MAIOR PUREZA DOS AÇOS. RINSSAGEM COM ARGÔNIO NO FORNO PANELA É UMAS DAS ETAPAS CRÍTICAS NA FABRICAÇÃO DE AÇO LIMPO, ESPECIALMENTE SE A RINSAGEM É EFETUADA ANTES DA ADIÇÃO DE CÁLCIO-SILÍCIO (DENOMINADA PRE-RINSAGEM). TESTES INDUSTRIAIS FORAM REALIZADOS NA VALLOUREC STAR (YOUNGSTOWN-ESTADOS UNIDOS). CORRIDAS FORAM PRODUZIDAS EM 2 CENÁRIOS DIFERENTES: COM E SEM A APLICAÇÃO DA PRE-RINSAGEM. AMOSTRAS LOLLIPOP ANALIZADAS EM ASPEX DEMONSTRARAM QUE CORRIDAS EM QUE A PRE-RINSAGEM FOI FEITA APRESENTARAM UMA REDUÇÃO NA DENSIDADE INCLUSIONAL EM 50% QUANDO COMPARADAS COM CORRIDAS EM QUE A PRE-RINSAGEM NÃO FOI EFETUADA (DENSIDADE DE INCLUSÕES ESTÁVEL). A PRÁTICA DE PRE-RINSAGEM FOI PADRONIZADA NA VALLOUREC STAR, APÓS OS RESULTADOS SATISFATÓRIOS DOS TESTES.
Steel cleanliness has become increasingly important throughout the years, bringing steelmaker’s attention to operational parameters that can optimize and fulfill these quality requirements. Argon stirring at the LMF is one of the key steps in achieving optimized steel cleanliness, especially if rinsing is performed before CaSi addition (pre-rinse). Trials were performed at Vallourec Star and heats were produced in 2 different scenarios: with and without pre-rinse. Lollipop samples analyzed via automated inclusion analysis (AIA) demonstrate that pre-rinsed heats presented a strong drop on inclusion density (by -50%) when compared to heats were not pre-rinsed (inclusion density remained stable). Pre-rinse practice was standardized at Vallourec Star.
Palavras-chave
metalurgia; rinsagem; inclusões não metálicas; forno panela
Steel cleanliness; Inclusions; Rinsing; LMF; Steelmaking
Como citar
Braga, Barbara Costa.
PADRONIZAçãO DE PRáTICAS DE RINSAGEM OBJETIVANDO OTIMIZAçãO DA LIMPIDEZ DO AçO
,
p. 642-655.
In: 52º Seminário de Aciaria, Fundição e Metalurgia de Não-Ferrosos,
São Paulo,
2023.
ISSN: 2594-5300
, DOI 10.5151/2594-5300-39645