Título

PASSIVAÇÃO DA CAL LIVRE PRESENTE EM ESCÓRIAS DE ACIARIA LD/BOF

PASSIVATION OF FREE LIME CONTAINED IN LD/BOF SLAG

Autoria

Dias, Naggme Hisse de Lima

Dias, Naggme Hisse de Lima

Eu sou esse autor

DOI

10.5151/2594-5327-34369

Downloads

Resumo

A SIDERURGIA BRASILEIRA GEROU EM 2019 APROXIMADAMENTE 5,0 MTON DE ESCÓRIAS VIA OS CONVERSORES LD/BOF. EMBORA ESSAS ESCÓRIAS SEJAM UTILIZADAS PELA ENGENHARIA CIVIL, AINDA EXISTEM SÉRIAS RESTRIÇÕES AO SEU USO, PRINCIPALMENTE DEVIDO À EXPANSÃO VOLUMÉTRICA OCASIONADA PELO CAO LIVRE. ESTUDOS DE CURA COM ÁGUA TEM MOSTRADO EFETIVIDADE NA REDUÇÃO DO EFEITO NEGATIVO DA CAL LIVRE. ESTE TRABALHO OBJETIVOU ACOMPANHAR, ALÉM DOS FENÔMENOS INERENTES À CURA DO CAO, VARIAÇÕES DE PH DAS ÁGUAS RESIDUAIS DA OPERAÇÃO DE UMECTAÇÃO. PARA TANTO, UTILIZANDO AMOSTRAS DE UMA USINA SIDERÚRGICA, EXPERIÊNCIAS DE BANCADA FORAM PLANEJADAS, SENDO PREPARADAS DUAS PILHAS DE ESCÓRIA PARA OS TRATAMENTOS DE UMECTAÇÃO, ATENDENDO PERÍODOS NÃO INFERIORES A 100 DIAS. AS TÉCNICAS UTILIZADAS PARA ACOMPANHAMENTO DA PASSIVAÇÃO FORAM A ANÁLISE QUÍMICA COM ETILENOGLICOL, TERMOGRAVIMETRIA-TG E ICP-OES. OS RESULTADOS MOSTRARAM DECLÍNIOS SIGNIFICATIVOS NO TEOR DA CAL LIVRE, DE 11,67% PARA 0,36% NO PERÍODO ESTUDADO DE 100 DIAS. A MESMA TENDÊNCIA DE QUEDA FOI OBSERVADA NOS VALORES DE PH DAS ÁGUAS RESIDUAIS, OS QUAIS, PARA OS DIAS ZERO E CENTÉSIMO DE TESTE, FORAM 12,57 E 10,65 RESPECTIVAMENTE. FINALMENTE, BUSCOU-SE COMPARAR OS RESULTADOS DO PRESENTE ESTUDO COM DADOS PRÁTICOS EXISTENTES PARA SITUAÇÕES “IN SITU”.

THE STEEL INDUSTRY IN BRAZIL GENERATED IN 2019 ABOUT 5,0 MTON OF SLAG FROM THE LD/BOF PROCESS. EVEN THOUGH THIS SLAG HAS BEEN UTILIZED ON CIVIL ENGINEERING PROJECTS THERE ARE STILL SEVERAL RESTRICTIONS ON ITS USE, MAINLY DUE TO THE VOLUMETRIC EXPANSION CAUSED BY THE FREE CAO. STUDIES ON CURING PROCESSES USING WATER HAVE SHOWN EFFECTIVITY ON THE REDUCTION OF THE NEGATIVE EFFECTS CAUSED BY FREE CAO. THIS WORK AIMED TO INVESTIGATE THE FREE CAO PASSIVATION REACTIONS AND THE PH VARIATION OF THE RESIDUAL WATER GENERATED FOR THE HUMECTATION PROCESS. IN SUCH WAY, USING SAMPLES FROM A STEEL MANUFACTURER, EXPERIMENTS WERE APPROPRIATELY PLANNED WHERE TWO SLAG STACKS WERE BEING PREPARED FOR THE AQUEOUS SOLUTIONS TREATMENT DURING THE PERIOD OF 100 DAYS. THE TECHNIQUES USED FOR MONITORING THE CALCIUM COMPOUNDS WERE THE CHEMICAL PROCEDURE USING ETHYLENE GLYCOL, THERMOGRAVIMETRY-TG AND ICP-OES. THE RESULTS SHOWED A DECREASE OF THE FREE LIME CONTENT FROM 11,67% TO 0,36% ALONG THE 100 DAYS AND THE PH REDUCTION FOR THE RESIDUAL WATER GENERATED DURING THE HUMECTATION PROCESS, FROM 12,57 TO 10,65, IN THE SAME PERIOD OF 100 DAYS. FINALLY, USING A DATABANK FOR “IN SITU” SLAG TREATMENT, WAS POSSIBLE AN USEFUL COMPARISON WITH THE RESULTS OBTAINED.

Palavras-chave

Cura; Cal livre; Escória de LD/BOF

Curing; Free lime; LD/BOF slag.