PREPARAÇÃO E CARACTERIZAÇÃO DE PÓS DO AÇO RÁPIDO AISI M2 COM ADIÇÃO DE NbC VIA MOAGEM DE ALTA ENERGIA

PROCESSING AND CHARACTERIZATION OF AISI M2 HIGH SPEED STEEL POWDERS WITH THE ADDITION OF NbC BY MECHANICAL ALLOYING

Autoria

Filho, Oscar Olimpio de Araujo; Filho, Cezar Henrique Gonzalez: Severino Leopoldino Urtiga; Neves, Mauricio David Martins das; Filho, Francisco Ambrozio

DOI

10.5151/2594-5327-14813

Downloads

Baixar Artigo 52 Downloads

Resumo

O objetivo do presente trabalho consiste na elaboração do aço rápido AISI M2 com adição de 6% de carboneto de nióbio (NbC) utilizando-se moagem de alta energia em um moinho Zoz do tipo Attritor horizontal. A relação bola:pó utilizada foi de 10:1 e os tempos de moagem foram de 5, 10 minutos e 1 hora. Estudou-se a influência dos tempos de moagem na morfologia das partículas usando-se Microscopia Eletrônica de Varredura (MEV) e por espectrometria de baixa energia dispersiva de raios X (EDS) objetivando a caracterização dos pós. A seguir os pós foram compactados uniaxialmente a frio e observou-se o encruamento dos mesmos no sentido de obter- se compactados isentos de trincas. Para todos os tempos de moagem o nióbio apresentou-se incrustado nas partículas do aço rápido M2, mas apresentaram-se excessivamente encruados e produziram trincas por ocasião da compactação. Medidas de teores de carbono e de oxigênio foram procedidas e apresentaram-se dentro do esperado.

 

Mechanical Alloying (MA) has been used primarily for particle size reduction, to its present status as an important method for the preparation of either materials with enhanced physical and mechanical properties or, indeed, new phases, or new engineering materials. In this work, Niobium carbide (NbC) was added to the AISI M2 HSS by Mechanical Alloying technique in an attritor mill and was characterized by means of SEM plus EDS. The milling times used were one hour, 10 and 5 minutes. The ball/powder ratio was 10:1.Then the powders were submitted to a suitable heat treatment of annealing either under vacuum and hydrogen atmospheres. The material which resulted from the milling procedure during one hour, 10 and 5 minutes was cold uniaxially compacted and it was observed cracks in all green compacts. The carbon and oxygen contents were obtained too. The sintering of the AISI M2 plus NbC will be discussed in a next work.

Palavras-chave

Metalurgia do pó; Moagem de alta energia; Caracterização microestrutural.

Powder metallurgy; Mechanical alloying; Microstructural characterization.