PREPARAÇÃO SUPERFICIAL DE LIGAS DE TITÂNIO PARA PARAFUSOS ORTODÔNTICOS

SUPERFICIAL PREPARATION OF TITANIUM ALLOYS FOR ORTHODONTIC SCREWS

Autoria

Batista, Peterson de Medeiros; Cardoso, Henrique Ribeiro Piaggio; Rodrigues, Luciana Machado; Schroeder, Roberto Moreira; Galio, Alexandre Ferreira; Müller, Iduvirges Lourdes

DOI

10.5151/2594-5327-16034

Downloads

Baixar Artigo 25 Downloads

Resumo

A adesão de implantes dentários pelo corpo humano esta intimamente ligada ao tratamento superficial ao qual o material do implante é submetido. Neste trabalho, avaliaram-se diferentes metodologias de preparação superficial de amostras de Ti para parafusos ortodônticos. A rugosidade superficial do material a ser implantado é um importante parâmetro para a efetiva adesão do implante de Ti ao osso. Foram realizados tratamentos superficiais os quais consistiram de lixamento e eletropolimento da superfície da amostra, visando a análise da rugosidade média obtida. No lixamento foram avaliadas diferentes granulometrias de lixas e no eletropolimento foram empregados diferentes parâmetros como composição e temperatura do banho, densidade de corrente e seu tempo de aplicação. Seguindo a preparação superficial, foi realizado ataque químico buscando-se os parâmetros ideais para a obtenção de aumento de rugosidade. Os resultados indicam que o valor de rugosidade média final, após o ataque químico, teve um acréscimo de aproximadamente 2μm. Pesquisas anteriores indicam que valores de rugosidade acima de 1,5μm são os recomendados para que o implante tenha uma boa adesão ao osso, portanto, o tratamento superficial aqui proposto tem sido eficiente.

 

The adhesion of dental implantations for the human body this closely on one to the superficial treatment which the material of the implantation is submitted. In this work, different methodologies of superficial preparation of Ti samples for orthodontic screws had been evaluated. The superficial rugosidade of to be implanted material is an important parameter for the effective adhesion of the Ti implantation to the bone. Superficial treatments had been carried through which had consisted of burnishing and electropolishing of the surface of the sample, aiming at the analysis of the gotten average roughness. In the burnishing different sizes of emery papers had been evaluated and in the electropolishing different parameters had been employees as composition and temperature of the bath, current density and its time of application. Following the superficial preparation, chemical attack was carried through searching the ideal parameters for the attainment of roughness increase. Following the superficial preparation, chemical attack was carried through searching the ideal parameters for the attainment of roughness increase. The results indicate that the final value of average roughness, after the chemical attack, had an addition of 2μm approximately. Previous research indicates that values of roughness above of 1,5μm are the recommended ones so that the implantation has a good adhesion in the bone, therefore, the superficial treatment considered here has been efficient.

Palavras-chave

Titânio; Implante; Tratamento superficial; Osseointegração.

Titanium; Implantation; Superficial treatment; Boneintegration.