Título

PROCESSAMENTO E CARACTERIZAÇÃO DE FILMES COMPÓSITOS DE FOSFATO DE CÁLCIO/ALGINATO/ÓXIDO DE GRAFENO (CAP-ALG-GO) PARA APLICAÇÕES EM BIOMATERIAIS

PROCESSING AND CHARACTERIZATION OF COMPOSITE FILMS BASED ON CALCIUM PHOSPHATE/ALGINATE/GRAPHENE OXIDE (CAP-ALG-GO) FOR BIOMATERIALS APPLICATIONS

Autoria

Alves, Lais de Souza; Lima, Andreza Menezes; Pinheiro, Wagner Anacleto; Ribeiro, Alexandre Antunes

DOI

10.5151/2594-5327-34919

Downloads

Baixar Artigo 14 Downloads

Resumo

FILMES POLIMÉRICOS CONTENDO FOSFATOS DE CÁLCIO, ÓXIDO DE GRAFENO, ALGINATO DE SÓDIO E COLÁGENO FORAM PRODUZIDOS ATRAVÉS DA TÉCNICA DE CASTING PARA POTENCIAL APLICAÇÃO EM BIOMATERIAIS. OS FILMES FORAM CARACTERIZADOS POR DRX, MEV, ESPECTROSCOPIA RAMAN E POR TESTES DE INTUMESCIMENTO PARA AVALIAR SEU COMPORTAMENTO EM AMBIENTE FISIOLÓGICO. NAS MICROSCOPIAS OBTIDAS POR MEV FOI POSSÍVEL NOTAR QUE A TÉCNICA UTILIZADA FOI BEM SUCEDIDA EM PRODUZIR FILMES HOMOGÊNEOS. OS RESULTADOS DE DIFRAÇÃO DE RAIOS–X MOSTRARAM A PRESENÇA DE ALGINATO, ÓXIDO DE GRAFENO E AS DUAS FASES DE FOSFATO DE CÁLCIO (HAP E Β-TCP), ASSIM COMO NA ANÁLISE DE RAMAN, ONDE SÃO IDENTIFICADAS AS BANDAS D E G, RELACIONADAS AO GRAFENO. A ADIÇÃO DE ÓXIDO DE GRAFENO NOS FILMES FOI CAPAZ DE REDUZIR A PRESENÇA DE FISSURAS E AUMENTAR O GRAU DE INTUMESCIMENTO E, CONSEQUENTEMENTE, A RESISTÊNCIA DOS FILMES À DEGRADAÇÃO.

 

POLYMERIC FILMS CONTAINING CALCIUM PHOSPHATES, GRAPHENE OXIDE, SODIUM ALGINATE AND COLLAGEN WERE PRODUCED USING THE CASTING TECHNIQUE FOR POTENTIAL APPLICATION IN BIOMATERIALS. FILMS WERE CHARACTERIZED BY XRD, SEM, RAMAN SPECTROSCOPY AND SWELLING TESTS TO ASSESS THEIR BEHAVIOR IN A PHYSIOLOGICAL ENVIRONMENT. IN THE MICROSCOPY OBTAINED BY SEM, IT WAS POSSIBLE TO NOTICE THAT THE TECHNIQUE USED WAS SUCCESSFUL IN PRODUCING HOMOGENEOUS FILMS. THE X-RAY DIFFRACTION RESULTS SHOWED THE PRESENCE OF ALGINATE, GRAPHENE OXIDE AND THE TWO PHASES OF CALCIUM PHOSPHATE (HAP E β-TCP), AS WELL AS IN THE RAMAN ANALYSIS, WHERE THE D AND G BANDS RELATED TO GRAPHENE ARE IDENTIFIED. THE ADDITION OF GRAPHENE OXIDE IN THE FILMS WAS ABLE TO REDUCE THE PRESENCE OF FISSURES AND INCREASE THE DEGREE OF SWELLING AND, CONSEQUENTLY, THE RESISTANCE OF THE FILMS TO DEGRADATION.

Palavras-chave

fosfato de cálcio; alginato; óxido de grafeno; compósitos; biomateriais.

calcium phosphate; alginate; graphene oxide; composites; biomaterials.