Título

PRODUÇÃO DE ALUMINA VIA ROTA SOL GEL PARA POSSÍVEL APLICAÇÃO EM BIOMATERIAIS

PRODUCTION OF ALUMINA VIA THE SOL GEL ROUTE FOR POSSIBLE APPLICATION IN BIOMATERIALS

Autoria

Nascimento, Damares da Cruz Barbosa; Matos, Taiana de Sousa; Paranhos, Sheila Barbosa; Monteiro, Sérgio Neves; Silva, Alisson Clay Rios da; Candido, Verônica Scarpini

DOI

10.5151/2594-5327-34992

Downloads

Baixar Artigo 8 Downloads

Resumo

AS QUESTÕES DE SAÚDE RELACIONADAS À QUALIDADE DA POPULAÇÃO ATUAL E EXPECTATIVA DE VIDA, APRESENTAM UMA DEMANDA MUITO IMPORTANTE PARA PESQUISA DE MATERIAIS BIOCOMPATÍVEIS E SEU APRIMORAMENTO. A ALUMINA É UMA BIOCERÂMICA QUE POSSUI CARACTERÍSTICAS DESEJÁVEIS DEVIDO SUA ALTA DUREZA, E RESISTÊNCIA À COMPRESSÃO E BOA BIOCOMPATIBILIDADE. NESTE TRABALHO CUJO OBJETIVO PRINCIPAL É PRODUZIR ALUMINA PARA POSSÍVEL APLICAÇÃO EM BIOMATERIAIS. A METODOLOGIA UTILIZADA PARA PRODUÇÃO DE ALUMINA FOI POR ROTA SOL-GEL A PREPARAÇÃO DO PÓ DE ALUMINA OCORREU A PARTIR DE 84 GRAMAS DE NITRATO DE ALUMÍNIO NONOHIDRATADO (AL(NO3)3.9H2O) MAIS 100 ML DE ÁGUA DESTILADA E 280 ML DE HIDRÓXIDO DE AMÔNIO (NH4OH) COMO AGENTE PRECIPITANTE, PARA POSTERIOR IMERSÃO EM ÁCIDO ACÉTICO (CH3COOH) A 40%, SEGUIDO DE TRATAMENTO TÉRMICO DE TRÊS HORAS EM 900ºC E MAIS TRÊS HORAS EM 1000°C RESULTANDO EM PÓ DE ALUMINA. A AMOSTRA FOI CARACTERIZADA POR DIFRAÇÃO DE RAIOS-X (DRX) E ESPECTROSCOPIA NA REGIÃO DO INFRAVERMELHO POR TRANSFORMADA DE FOURIER (FTIR). OS RESULTADOS INDICARAM QUE O MATERIAL OBTEVE Α- AL2O3 FASE MAIS ESTÁVEL TERMODINAMICAMENTE DO MATERIAL, MAS TAMBÉM CARACTERÍSTICAS DE CRISTALINIDADE ALÉM DE BANDAS VIBRACIONAIS CARACTERÍSTICAS.

 

HEALTH ISSUES RELATED TO THE QUALITY OF THE CURRENT POPULATION AND LIFE EXPECTANCY PRESENT A VERY IMPORTANT DEMAND FOR RESEARCH ON BIOCOMPATIBLE MATERIALS AND THEIR IMPROVEMENT. ALUMINA IS A BIOCERAMIC THAT HAS DESIRABLE CHARACTERISTICS DUE TO ITS HIGH HARDNESS, COMPRESSIVE STRENGTH AND GOOD BIOCOMPATIBILITY. IN THIS WORK WHOSE MAIN OBJECTIVE IS TO PRODUCE ALUMINA FOR POSSIBLE APPLICATION IN BIOMATERIALS. THE METHODOLOGY USED FOR THE PRODUCTION OF ALUMINA WAS BY SOL-GEL ROUTE, THE PREPARATION OF THE ALUMINA POWDER OCCURRED FROM 84 GRAMS OF NON-HYDRATED ALUMINUM NITRATE (AL(NO3)3.9H2O) PLUS 100 ML OF DISTILLED WATER AND 280 ML OF HYDROXIDE AMMONIUM (NH4OH) AS A PRECIPITATING AGENT, FOR SUBSEQUENT IMMERSION IN ACETIC ACID (CH3COOH) AT 40%, FOLLOWED BY HEAT TREATMENT FOR THREE HOURS AT 900ºC AND ANOTHER THREE HOURS AT 1000ºC, RESULTING IN ALUMINA POWDER. THE SAMPLE WAS CHARACTERIZED BY X-RAY DIFFRACTION (XRD) AND FOURIER TRANSFORM INFRARED SPECTROSCOPY (FTIR). THE RESULTS INDICATED THAT THE MATERIAL OBTAINED THE MOST THERMODYNAMICALLY STABLE α- AL2O3 PHASE OF THE MATERIAL, BUT ALSO CRYSTALLINITY CHARACTERISTICS IN ADDITION TO CHARACTERISTIC VIBRATIONAL BANDS.

Palavras-chave

Biocerâmicas; Temperatura; α- Al2O3

Bioceramics; Temperature; α- Al2O3