PRODUÇÃO DE PEÇAS DE AÇO MARAGING 300 POR FUSÃO SELETIVA A LASER A PARTIR DE PÓ PRODUZIDO NACIONALMENTE

PRODUCTION OF MARAGING 300 STEEL PARTS BY SELECTIVE LASER MELTING FROM NATIONALLY PRODUCED POWDER

Autoria

Souza, Carolina Alencar Caldeira de; Sousa, Talita Gama de; Gomes, Alaelson Vieira; Jardini, André Luiz; Souza, Eduardo Netto de; Brandao, Luiz Paulo Mendonca

DOI

10.5151/2594-5327-34929

Downloads

Baixar Artigo 13 Downloads

Resumo

A FUSÃO SELETIVA A LASER É UM PROCESSO DE MANUFATURA ADITIVA (MA) EM QUE É REALIZADA A FUSÃO SELETIVA DE UM LEITO PÓ, SENDO ESTE PÓ MUITAS VEZES IMPORTADO E PRÉ-DETERMINADO POR FABRICANTES DOS EQUIPAMENTOS UTILIZADOS. ESTE TRABALHO OBJETIVOU A PRODUÇÃO DE PEÇAS POR MA A PARTIR DE PÓS DE AÇO MARAGING 300 PRODUZIDOS NACIONALMENTE ATRAVÉS DE ATOMIZAÇÃO A GÁS. FORAM REALIZADAS ANÁLISES POR MEV E DRX DO PÓ E UMA AVALIAÇÃO VISUAL DA INTEGRIDADE DAS PEÇAS PRODUZIDAS POR MA. FOI POSSÍVEL OBTER AMOSTRAS DE PÓ COM PARTÍCULAS DE MORFOLOGIA ESFÉRICA E IRREGULAR COM TAMANHOS DESDE 5 ATÉ 80 ΜM. NOTOU-SE UMA INTEGRIDADE VISUAL DAS PEÇAS PRODUZIDAS POR MA E O PROCESSO OCORREU SEM INTERRUPÇÕES. CONCLUIU-SE, QUE O TAMANHO DAS PARTÍCULAS ESTAVA DE ACORDO COM A LITERATURA E, PELOS RESULTADOS DO PROCESSO DE MA, HÁ INDÍCIOS DE QUE OS PARÂMETROS E PÓ UTILIZADOS FORAM ADEQUADOS AO PROCESSO.

 

SELECTIVE LASER MELTING IS AN ADDITIVE MANUFACTURING PROCESS (AM) IN WHICH THE SELECTIVE FUSION OF A POWDER BED IS CARRIED OUT, THIS POWDER BEING OFTEN IMPORTED AND PREDETERMINED BY THE MANUFACTURERS OF THE EQUIPMENT USED. THIS WORK AIMED TO PRODUCE PARTS BY MA FROM MARAGING 300 STEEL POWDERS PRODUCED NATIONALLY THROUGH GAS ATOMIZATION. ANALYZES BY SEM AND XRD OF THE POWDER AND A VISUAL EVALUATION OF THE INTEGRITY OF THE PARTS PRODUCED BY AM WERE CARRIED OUT. IT WAS POSSIBLE TO OBTAIN POWDER SAMPLES WITH PARTICLES OF SPHERICAL AND IRREGULAR MORPHOLOGY WITH SIZES FROM 5 TO 80 µM. THERE WAS A VISUAL INTEGRITY OF THE PIECES PRODUCED BY AM AND THE PROCESS TOOK PLACE WITHOUT INTERRUPTIONS. IT WAS CONCLUDED THAT THE PARTICLE SIZE WAS IN AGREEMENT WITH THE LITERATURE AND, ACCORDING TO THE RESULTS OF THE AM PROCESS, THERE IS EVIDENCE THAT THE PARAMETERS AND POWDER USED WERE ADEQUATE FOR THE PROCESS.

Palavras-chave

Manufatura Aditiva; Fusão Seletiva a Laser; Aço Maraging.

Additive Manufacturing; Selective Laser Melting; Maraging Steel.