PROPRIEDADES MECÂNICAS E MICROESTRUTURA DE METAIS DE SOLDA DE ALTA RESISTÊNCIA OBTIDOS PELOS PROCESSOS GMAW E SMAW

MECHANICAL PROPERTIES AND MICROSTRUCTURE OF HIGH STRENGTH STEEL WELD METALS OBTAINED BY GMAW AND SMAW PROCESSES

Autoria

Gomes, Antonio José de Carvalho; Queiroz, Samuel Soares; Jorge, Jorge Carlos Ferreira; Souza, Luís Felipe Guimarães de; Mendes, Matheus Campolina; Araujo, Leonardo Sales

DOI

10.5151/1516-392X-30429

Downloads

Baixar Artigo 373 Downloads

Resumo

O presente trabalho apresenta uma análise comparativa entre as propriedades mecânicas dos metais de solda de aço de alta resistência obtidos pelos processos eletrodo revestido (SMAW) e Gas Metal Arc Welding (GMAW). Foram realizadas soldagens multipasses pelos processos SMAW e GMAW, com preaquecimento de 200°C, posição plana e energia de soldagem média de 1,49kJ/mm para o processo SMAW e 1,33kJ/mm para o processo GMAW. Após a soldagem, realizou-se um tratamento térmico a 600°C durante 1 hora, sendo esta condição comparada com a condição de como soldada. Foram realizados ensaios de tração, Charpy-V, dureza e metalográficos por microscopia eletrônica de varredura para caracterização mecânica e microestrutural dos metais de solda. Os resultados mostraram que ambos os processos propiciaram boas propriedades mecânicas para todas as condições.

 

The present work presents a comparative analysis between the mechanical properties of high strength steel weld metals obtained by the shielded metal arc (SMAW) and gas metal arc welding (GMAW) processes. Multipass welding by SMAW and GMAW processes were performed with preheating of 200°C, in the flat position and average energy welding of 1.49kJ/mm for SMAW and 1.33kJ/mm for GMAW process. After welding a post weld heat treatment at 600°C for 1 hour was performed, this condition being compared with the as welded condition. Tensile, Charpy-V notch, hardness tests and metallographic examination by scanning electron microscopy were performed for mechanical and microstructural characterization. The results showed that good mechanical properties were obtained in all conditions for both processes.

Palavras-chave

Metal de solda, Propriedades mecânicas, Tratamento térmico.

Weld metal, Mechanical properties, Heat treatment.