Título

PROPRIEDADES MECÂNICAS DE COMPÓSITOS DE RESINA EPÓXI REFORÇADA COM ESCAMAS DE PIRARUCU

MECHANICAL PROPERTIES OF ARAPAIMA SCALES REINFORCED EPOXY COMPOSITES

Autoria

Bezerra, Wendell Bruno Almeida; Costa, Ulisses Oliveira; Oliveira, Michelle Souza; Demosthenes, Luana Cristyne da Cruz; Luz, Fernanda Santos da; Filho, Fabio da Costa Garcia; Monteiro, Sergio Neves

DOI

10.5151/2594-5327-34145

Downloads

Baixar Artigo 29 Downloads

Resumo

A RESSIGNIFICAÇÃO DE MATERIAIS NATURAIS PARA APLICAÇÕES DE MAIOR DEMANDA TECNOLÓGICA É UMA ABORDAGEM ECONOMICAMENTE ATRATIVA PARA O DESENVOLVIMENTO DE NOVOS MATERIAIS SUSTENTÁVEIS. DESSA FORMA, A UTILIZAÇÃO DE MATERIAIS NATURAIS COMO REFORÇOS EM COMPÓSITOS SURGE COM UM GRANDE POTENCIAL. ESTE TRABALHO SE PROPÔS A ANALISAR AS PROPRIEDADES MECÂNICAS ESTÁTICAS E DINÂMICAS DE COMPÓSITOS DE RESINA EPÓXI REFORÇADA COM ESCAMAS DE PIRARUCU. OS COMPÓSITOS FORAM PREPARADOS UTILIZANDO 20, 30 E 40%VOL DE ESCAMAS DE PIRARUCU E FORAM ANALISADOS ATRAVÉS DE ENSAIOS DE IMPACTO IZOD, ENSAIO DE COMPRESSÃO E ANÁLISE DA ABSORÇÃO DE ENERGIA DE IMPACTO POR VELOCIDADE RESIDUAL. OS RESULTADOS DE IMPACTO IZOD DEMONSTRARAM UM AUMENTO SIGNIFICATIVO NA ENERGIA ABSORVIDA PARA OS COMPÓSITOS COM 40%VOL DE ESCAMAS, ENQUANTO OS COM 20% NÃO DEMONSTRARAM ALTERAÇÃO CONSIDERÁVEL. OS ENSAIOS DE COMPRESSÃO DOS COMPÓSITOS COM 30%VOL DE ESCAMAS DEMONSTRARAM UM AUMENTO SIGNIFICATIVO NO MÓDULO DE ELASTICIDADE E NA RESISTÊNCIA À COMPRESSÃO, EM RELAÇÃO À RESINA PURA, BEM COMO NO ENSAIO DE VELOCIDADE RESIDUAL HOUVE UM AUMENTO NA ENERGIA ABSORVIDA PELO COMPÓSITO COM A INCORPORAÇÃO DAS ESCAMAS DE PIRARUCU NA RESINA EPÓXI.

 

THE REPURPOSING OF NATURAL MATERIALS FOR APPLICATIONS WITH GREATER TECHNOLOGICAL DEMAND IS AN ECONOMICALLY ATTRACTIVE APPROACH TO THE DEVELOPMENT OF NEW SUSTAINABLE MATERIALS. THUS, THE USE OF NATURAL MATERIALS AS REINFORCEMENT IN COMPOSITES ARISES WITH GREAT POTENTIAL. THIS WORK PROPOSED TO ANALYZE STATIC AND DYNAMIC MECHANICAL PROPERTIES OF ARAPAIMA SCALES REINFORCED EPOXY COMPOSITES. THE COMPOSITES WERE PREPARED USING 20, 30 AND 40VOL% ARAPAIMA SCALES AND WERE ANALYZED USING IZOD IMPACT TESTS, COMPRESSION TESTS AND BALLISTIC ANALYSIS OF IMPACT ENERGY ABSORPTION BY RESIDUAL VELOCITY. THE RESULTS OF IZOD IMPACT TESTS DEMONSTRATED A SIGNIFICANT INCREASE IN THE ABSORBED ENERGY FOR THE 40VOL%COMPOSITES E, WHILE THE 20% DID NOT A CONSIDERABLE CHANGE. COMPRESSION TESTS OF THE 30VOL% COMPOSITES DEMONSTRATED A SIGNIFICANT INCREASE IN THE YOUNG MODULUS AND COMPRESSIVE STRENGTH, AS COMPARED TO THE PLAIN EPOXY. A SIMILAR RESULT WAS SEEN IN RESIDUAL VELOCITY TESTS, WHERE AN INCREASE IN THE ABSORBED IMPACT ENERGY WAS OBSERVED WITH THE INCORPORATION OF THE 30VOL% OF ARAPAIMA SCALES IN EPOXY RESIN.

Palavras-chave

Escamas; Compósitos; Velocidade residual; Propriedades mecânicas

Arapaima scales; Epoxy composites; Residual velocity; Mechanical properties