QUANTIFICAÇÃO DA FASE SIGMA EM AÇO SUPERDUPLEX SUBMETIDO A DIFERENTES TRATAMENTOS TÉRMICOS

QUANTIFICATION OF SIGMA PHASE IN SUPERDUPLEX STEEL UNDER DIFFERENT HEAT TREATMENTS

DOI

10.5151/2594-5327-21117

Downloads

Baixar Artigo 504 Downloads

Resumo

Aços inoxidáveis do tipo duplex são largamente utilizados na indústria petroquímica devido à união de boas propriedades mecânicas e resistência à corrosão. Quando submetidos a temperaturas elevadas, os aços do tipo duplex tendem a precipitar fases deletérias, que prejudicam suas propriedades. Este trabalho avaliou a influência da temperatura na quantidade de fase sigma precipitada. Seis amostras do aço inoxidável superduplex UNS S32750 foram retiradas de uma barra redonda laminada. Uma permaneceu na condição como recebida e as demais foram tratadas termicamente, cada uma das cinco, a 800°C, 850°C, 900°C, 950°C e 1.000°C, por 30 minutos, com posterior resfriamento em água. As amostras foram preparadas metalograficamente pelas técnicas de lixamento e polimento. Sendo posteriormente atacadas eletroliticamente com solução de NaOH. As imagens obtidas por microscopia óptica foram processadas pelo programa ImLab, utilizando a técnica de processamento digital de imagens para quantificação do percentual das fases presentes. As micrografias revelaram o aparecimento da fase sigma, além da presença já esperada de ferrita e austenita. Após os resultados do processamento digital de imagens, estabeleceu-se uma relação entre a temperatura do tratamento térmico e a quantidade de fase sigma precipitada.

 

Duplex stainless steels are widely used in petrochemical industry due to the union of good mechanical properties and corrosion resistance. When submitted to high temperatures, the duplex stainless steels tend to precipitate deleterious phases, which affect their properties. This work evaluated the influence of the temperature on the amount of sigma phase precipitated. Six samples of the superduplex stainless steel UNS S32750 were withdrawn from a laminated round bar. One remained as in the received condition and the others were treated thermally, each of the five, at 800°C, 850°C, 900°C, 950°C and 1,000°C, for 30 minutes, with subsequent cooling in water. The samples were metallographically prepared by grinding and polishing techniques. Being subsequently attacked electrolytically with NaOH solution. The obtained images by optical microscopy were processed by ImLab software, using the digital image processing technique to quantify the percentage of present phases. The micrographs revealed the emergence of sigma phase, and an expected presence of ferrite and austenite. After the results of digital image processing, was settled a relation between the heat treatment temperature and the amount of sigma phase precipitated.

Palavras-chave

Superduplex; Microscopia óptica; Processamento digital de imagens.

Superduplex; Optical microscopy; Digital image processing.

Como citar

Nunes, Thalyta Martins de Avelar; Pimenta, André Rocha; Diniz, Marilia Garcia; Dias, Débora Francielle. QUANTIFICAÇÃO DA FASE SIGMA EM AÇO SUPERDUPLEX SUBMETIDO A DIFERENTES TRATAMENTOS TÉRMICOS , p. 1584-1594. In: 67º Congresso da ABM - Internacional / 12º ENEMET - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas, Rio de Jabeiro, 2012.