QUANTIFICAÇÃO DE FASE DE LIGA DE ALTA ENTROPIA ALCO2CR2FENI2 FUNDIDA E TRATADA

PHASE QUANTIFICATION OF THE ALCO2CR2FENI2 HIGH ENTROPY ALLOY CASTING AND HEAT TREATED

DOI

10.5151/2594-5327-34670

Downloads

Baixar Artigo 13 Downloads

Resumo

DE ESTRUTURAS RELATIVAMENTE SIMPLES E COM VASTA POSSIBILIDADE DE COMBINAÇÕES DE ELEMENTOS E CONSEQUENTEMENTE DE PROPRIEDADES, DIVERSAS LIGAS METÁLICAS VÊM SENDO DESENVOLVIDAS E ESTUDADAS DESDE O SÉCULO PASSADO E NESTE NOVO MILÊNIO DESTACAM-SE AS LIGAS DE ALTA DE ALTA ENTROPIA (LAE), EM ESPECIAL SE DESTACA O SISTEMA DE LIGAS AL-CO-CR-FE-NI, QUE GANHA DESTAQUE POR SUA RESISTÊNCIA A CORROSÃO E MECÂNICA, E BAIXA DENSIDADE. O PRESENTE ESTUDO TEM POR OBJETIVO QUANTIFICAR AS FASES PRESENTES DA LIGA ALCO2CR2FENI2, NAS REGIÕES DENDRÍTICA E INTERDENDRÍTICA, COMO FUNDIDA E TRATADA TERMICAMENTE (1050 ºC POR 1 HORA SEGUIDO DE RESFRIAMENTO EM ÁGUA), COM AUXÍLIO DA MICROSCOPIA ÓPTICA E ELETRÔNICA DE VARREDURA. EVIDENCIOU-SE CERCA DE 80% DA MICROESTRUTURA É CONSTITUÍDA DE REGIÃO DENDRÍTICA E 20% DE REGIÃO INTERDENDRÍTICA EM AMBAS AS CONDIÇÕES DE PROCESSAMENTO PARA LIGA EM ESTUDO, APENAS DIFERENCIANDO O ASPECTO MICROESTRUTURAL NA CONDIÇÃO TRATADA PELA FORMAÇÃO DE PRECIPITADOS EM FORMA DE BASTONETES EM AMBAS AS REGIÕES.

 

OF RELATIVELY SIMPLE STRUCTURES AND WITH A WIDE POSSIBILITY OF ALLOY ELEMENTS COMBINATIONS AND CONSEQUENTLY OF PROPERTIES, SEVERAL METALLIC ALLOYS HAVE BEEN DEVELOPED AND STUDIED SINCE THE LAST CENTURY AND IN THIS NEW MILLENNIUM THE HIGH ENTROPY HIGH ALLOYS (HEA) STAND OUT, ESPECIALLY IF HIGHLIGHTS THE AL-CO-CR-FE-NI ALLOY SYSTEM, WHICH STANDS OUT FOR ITS RESISTANCE TO CORROSION AND MECHANICS, AND LOW DENSITY. THE PRESENT WORK AIMS TO QUANTIFY THE PRESENT PHASES OF THE ALCO2CR2FENI2 ALLOY, DENDRITIC AND INTER-DENDRITIC REGIONS, AS CASTED AND HEAT TREATED (1050 ºC FOR 1 HOUR, FOLLOWED BY COOLING IN WATER) AID BY OPTICAL MICROSCOPY AND SCANNING ELECTRON MICROSCOPY. IT WAS FOUND THAT ABOUT 80% OF THE MICROSTRUCTURE CONSISTS OF DENDRITIC REGION AND ABOUT 20% IS INTER-DENDRITIC REGION IN BOTH OF SAMPLES, ONLY DIFFERENTIATING THE MICROSTRUCTURAL ASPECT IN THE CONDITION TREATED BY THE FORMATION OF ROD-SHAPED PRECIPITATES IN BOTH REGIONS.

Palavras-chave

Liga de Alta Entropia; Quantificação de Fase; Metalografia; Tratamento Térmico.

High Entropy Alloy; Phase quantification; Metallography; Heat Treatment.