Anais do Enemet - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas


ISSN 2594-4711

Título

RESISTÊNCIA À CORROSÃO DE FILMES HÍBRIDOS APLICADOS SOBRE FOLHAS DE FLANDRES: SOLUÇÃO PRECURSORA ACIDIFICADA COM ÁCIDO NÍTRICO (pH=3)

CORROSION RESISTANCE OF HYBRID FILMS APPLIED ON TIN PLATE: PRECURSOR SOLUTION ACIDIFIED WITH NITRIC ACID (pH=3)

DOI

10.5151/2594-4711-23047

Downloads

Baixar Artigo 255 Downloads

Resumo

Os pré-tratamentos baseados nos sistemas siloxano-PMMA têm mostrado resultados promissores atraindo também a atenção das indústrias nos últimos anos, pois esses revestimentos híbridos melhoram as características de proteção contra a corrosão das folhas de flandres e as propriedades de adesão dos revestimentos orgânicos sobre esse substrato, além de provocar menores impactos ambientais comparados à cromatização. O objetivo do presente trabalho é revestir as folhas de flandres com um filme híbrido obtido a partir de um sol constituído pelos precursores alcoóxidos: 3-(trimetoxisililpropil)metacrilato (TMSM), poli(metacrilato de metila) PMMA e tetraetoxisilano (TEOS) variou-se em três níveis a concentração de TEOS (1, 2 e 3). Os filmes foram obtidos pelo processo de dipcoating e tratados termicamente por 3 horas numa temperatura de 160°C. Avaliou-se a hidrofobicidade dos revestimentos através de medidas de ângulo de contato. Os filmes híbridos obtidos foram caracterizados quanto ao comportamento eletroquímico e morfológico. Os resultados mostraram que o filme híbrido siloxano-PMMA com maior concentração de TEOS apresentou maior espessura, no entanto, devido à intensa densificação do filme promovida pela adição de TEOS, houve a formação de fissuras, comprometendo desse modo a resistência à corrosão.

 

Pretreatments systems based on siloxane-PMMA have shown promising results also attracting the attention of industries in recent years because these hybrid coatings improve the characteristics of corrosion protection of tin plates and the adhesion properties of organic coatings on this substrate, and cause less environmental impacts compared to chromating. The aim of this work is to coat tin plate with a hybrid film obtained from a sol consisting of alkoxide precursors: 3 - (trimethoxysilylpropyl) methacrylate (TMSM), poly (methyl methacrylate) PMMA with tetraethoxysilane (TEOS) was varied in three levels, the concentration of TEOS (1, 2 and 3). The films were obtained by dip-coating process, cured for 3 hours at 160°C. The film hydrophobicity was determined by the contact angle measurements. The hybrid films were characterized as the morphological and electrochemical behavior. The results showed that the hybrid film siloxane-PMMA with a higher concentration of TEOS showed increased thickness, however, due to the intense densification of the film promoted by the addition of TEOS, there was the formation of cracks, thereby compromising the corrosion resistance.

Palavras-chave

Silanos; Ácido nítrico; Folha de flandres; Corrosão; TEOS.

Silanes; Nitric acid; Tinplate; Corrosion; TEOS.

Como citar

Kunst, Sandra Raquel; Bertoli, Paloma; Parise, Karine; Ludwig, Gustavo; Muller, Iduvirges Lourdes; Malfatti, Célia de Fraga. RESISTÊNCIA À CORROSÃO DE FILMES HÍBRIDOS APLICADOS SOBRE FOLHAS DE FLANDRES: SOLUÇÃO PRECURSORA ACIDIFICADA COM ÁCIDO NÍTRICO (pH=3) , p. 150-158. In: 13º ENEMET - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas, São Paulo - Brasil, 2013.
ISSN: 2594-4711 , DOI 10.5151/2594-4711-23047