RESISTÊNCIA À CORROSÃO DE REVESTIMENTOS GALVANIZADOS PASSIVADOS EM ESCALA PILOTO COM DIFERENTES MASSAS DE CROMO TRIVALENTE: CORROSION RESISTANCE OF PILOT-SCALE PASSIVATED GALVANIZED COATINGS WITH DIFFERENT TRIVALENT CHROMIUM WEIGHTS

O ROLL COATER é O DISPOSITIVO MAIS INDICADO PARA APLICAçãO DE FILMES FINOS NA SUPERFíCIE DE AçOS PLANOS, POIS APRESENTA MAIOR PRECISãO QUE APLICAçõES POR IMERSãO OU PULVERIZAçãO, ALéM DE EXIGIR MENOR CONSUMO DE INSUMOS E TRATAMENTO DE EFLUENTES. RECENTEMENTE, O CENTRO DE PESQUISA E DESENVOLVIMENTO DA USIMINAS ADQUIRIU UM ROLL COATER PARA APRIMORAR A APLICAçãO DE PóS-TRATAMENTOS EM ESCALA PILOTO. NESTE ESTUDO SãO APRESENTADOS OS RESULTADOS OBTIDOS PARA UM AçO GALVANIZADO (GI) PASSIVADO COM CROMO TRIVALENTE UTILIZANDO ESTE EQUIPAMENTO. FORAM PRODUZIDOS FILMES PASSIVANTES COM VáRIOS MASSAS DE CROMO E AVALIADA A RELAçãO DESTE PARâMETRO COM A PROTEçãO CONTRA A OXIDAçãO PRECOCE DO ZINCO DURANTE A EXPOSIçãO EM CâMARA DE NéVOA SALINA. OS REVESTIMENTOS COM MENOS DE 14 MG/M2 DE CROMO NãO PROPORCIONARAM PROTEçãO SATISFATóRIA, ENQUANTO AQUELES COM 21 MG/M2, QUE ESTá DENTRO DA FAIXA RECOMENDADA PELO FORNECEDOR DO PASSIVADOR, ATENDERAM AO REQUISITO DE MENOS DE 5% DE áREA COM CORROSãO BRANCA APóS 48 HORAS DE TESTE DE NéVOA SALINA. VERIFICOU-SE TAMBéM QUE A HOMOGENEIDADE DO FILME PASSIVANTE é EXTREMAMENTE IMPORTANTE PARA UM BOM DESEMPENHO CONTRA A CORROSãO. ALéM DISSO, FILMES MUITO ESPESSOS TENDEM A CRAQUELAR E DESPLACAR, EXPONDO O ZINCO EM MICRORREGIõES E, CONSEQUENTEMENTE, PROMOVENDO SUA OXIDAçãO PREMATURA.

THE ROLL COATER IS THE MOST SUITABLE APPLICATION DEVICE FOR OBTAINING THIN FILMS ON FLAT STEEL SURFACE, AS IT PRESENTS GREATER PRECISION THAN IMMERSION OR SPRAY APPLICATIONS, IN ADDITION TO REQUIRING LESS INPUTS CONSUMPTION AND EFFLUENT TREATMENT. RECENTLY, THE RESEARCH AND DEVELOPMENT CENTER OF USIMINAS ACQUIRED A ROLL COATER TO IMPROVE THE PILOT-SCALE POST-TREATMENT APPLICATION. IN THIS STUDY THE RESULTS OBTAINED FOR A GALVANIZED STEEL (GI) PASSIVATED WITH CHROMIUM TRIVALENT USING THIS EQUIPMENT ARE PRESENTED. PASSIVATING FILMS WITH VARIOUS CHROMIUM WEIGHTS WERE PRODUCED AND THE RELATIONSHIP OF THIS PARAMETER WITH THE PROTECTION AGAINST ZINC EARLY OXIDATION DURING EXPOSURE IN A SALT SPRAY CHAMBER WAS EVALUATED. THE COATINGS WITH LESS THAN 14 MG/M2 OF CHROMIUM DID NOT PROVIDE SATISFACTORY PROTECTION, WHILE THOSE WITH 21 MG/M2, WHICH IS WITHIN THE RANGE RECOMMENDED BY THE PASSIVATOR’S SUPPLIER, MET THE REQUIREMENT OF LESS THAN 5% OF AREA WITH WHITE CORROSION AFTER 48 H OF SALT SPRAY TEST. IT WAS ALSO FOUNDED THAT THE PASSIVATING FILM HOMOGENEITY IS EXTREMELY IMPORTANT FOR A GOOD PERFORMANCE AGAINST CORROSION. FURTHERMORE, VERY THICK FILMS TENDED TO CRACK AND FLAKE OFF, EXPOSING THE ZINC IN MICROREGIONS AND, CONSEQUENTLY, PROMOTING ITS PREMATURE OXIDATION.

Palavras-chave

ESCALA PILOTO; PASSIVAÇÃO; AÇO GALVANIZADO; CORROSÃO

Pilot-scale; Passivation; Galvanized steel; Corrosion.

Como citar

GUIMARAES, JULIANA PORTO; MARTINS, BRUNA GONÇALVES; PIMENTA, EGNALDA PEREIRA DA SILVA; PIMENTA, EGNALDA PEREIRA DA SILVA. RESISTÊNCIA À CORROSÃO DE REVESTIMENTOS GALVANIZADOS PASSIVADOS EM ESCALA PILOTO COM DIFERENTES MASSAS DE CROMO TRIVALENTE , p. 61-68. In: 59º Seminário de Laminação, Conformação de Metais e Produtos, São Paulo, Brasil, 2024.
ISSN: 2594-5297 , DOI 10.5151/2594-5297-40503