RESISTÊNCIA À FADIGA EM CANAL DENTÁRIO ARTIFICIAL DE FIOS DE NITI

NITI WIRES RESISTANCE TO FATIGUE IN ARTIFICIAL DENTAL CANAL

Autoria

GARCIA, JULIANNA MAGALHÃES; SANTOS, IVI COSTA ROCHA DOS; NASCIMENTO, MARVIN DO; VIEIRA, VICTOR TALARICO LEAL; ELIAS, CARLOS NELSON

GARCIA, JULIANNA MAGALHÃES

Eu sou esse autor

SANTOS, IVI COSTA ROCHA DOS

Eu sou esse autor

NASCIMENTO, MARVIN DO

Eu sou esse autor

VIEIRA, VICTOR TALARICO LEAL

Eu sou esse autor

ELIAS, CARLOS NELSON

Eu sou esse autor

DOI

10.5151/2594-5327-41210

Downloads

Resumo

AS LIGAS DE NITI USADAS NA FABRICAçãO DE INSTRUMENTOS PARA TRATAMENTO DE CANAIS DENTáRIOS E ORTODONTIA POSSUEM SUPERELASTICIDADE E BAIXO MóDULO DE ELASTICIDADE. ESTAS LIGAS FACILITAM O TRATAMENTO DE CANAIS RADICULARES COM CURVATURA ACENTUADA E A MOVIMENTAçãO DOS DENTES NOS TRATAMENTOS ORTODôNTICOS. NO PRESENTE TRABALHO DETERMINOU-SE A RESISTêNCIA à FADIGA DE FIOS DE NITI. OS FIOS DE NITI SEM E COM RANHURAS A 0°, 30°, 60° E 90° EM RELAçãO AO COMPRIMENTO FORAM SUBMETIDOS A ENSAIOS DE FADIGA SIMULANDO AS CONDIçõES DE USO CLíNICO. OS RESULTADOS MOSTRARAM QUE OS FIOS COM RANHURAS A 30° APRESENTAM MENOR VIDA úTIL. AS SUPERFíCIES DE FRATURA EXIBIRAM CARACTERíSTICAS PREDOMINANTEMENTE DúCTEIS COM A FORMAçãO DE MICROCAVIDADES ASSOCIADAS AOS ENSAIOS DE FADIGA. OS RESULTADOS OBTIDOS SãO IMPORTANTES PARA COMPREENDER O COMPORTAMENTO DOS INSTRUMENTOS DE NITI SOB FADIGA, ORIENTAM OS CLíNICOS NA SELEçãO E USO SEGURO DOS INSTRUMENTOS NA PRáTICA CLíNICA E SERVEM DE SUBSíDIOS AOS FABRICANTES PARA MELHORAR A FABRICAçãO

NITI ALLOYS USED TO MANUFACTURE INSTRUMENTS FOR TREATING DENTAL CANALS AND ORTHODONTICS HAVE SUPERELASTICITY AND A LOW MODULUS OF ELASTICITY. THESE ALLOYS FACILITATE THE TREATMENT OF ROOT CANALS WITH PRONOUNCED CURVATURE AND THE MOVEMENT OF TEETH DURING ORTHODONTIC TREATMENTS. IN THE PRESENT WORK, THE FATIGUE RESISTANCE OF NITI WIRES WAS DETERMINED. NITI WIRES WITHOUT AND WITH GROOVES AT 0°, 30°, 60°, AND 90° IN THE LENGTH DIRECTION WERE SUBJECTED TO FATIGUE TESTS SIMULATING CLINICAL USE CONDITIONS. THE RESULTS SHOWED THAT WIRES WITH GROOVES AT 30° HAVE A SHORTER USEFUL LIFE. THE FRACTURE SURFACES EXHIBITED PREDOMINANTLY DUCTILE CHARACTERISTICS WITH THE FORMATION OF MICROCAVITIES ASSOCIATED WITH FATIGUE TESTS. THE RESULTS OBTAINED ARE ESSENTIAL FOR UNDERSTANDING THE BEHAVIOR OF NITI INSTRUMENTS UNDER FATIGUE. THEY GUIDE CLINICIANS IN SELECTING AND SAFELY USING INSTRUMENTS IN CLINICAL PRACTICE AND SERVE AS INPUT FOR MANUFACTURERS TO IMPROVE MANUFACTURING.

Palavras-chave

Fadiga; Fios de NiTi; Fratura; Transformação de Fases

Fatigue; NiTi Wires; Fracture; Phase Transformation