RESPOSTA AO TRATAMENTO TÉRMICO DE TÊMPERA E REVENIMENTO PARA O FERRO FUNDIDO BRANCO DO TIPO ASTM A532

RESPONSE TO QUENCHING AND TEMPERING HEAT TREATMENT FOR ASTM A532 TYPE WHITE CAST IRON

Autoria

PINEDO, CARLOS EDUARDO; MAGNABOSCO, RODRIGO

PINEDO, CARLOS EDUARDO

Eu sou esse autor

MAGNABOSCO, RODRIGO

Eu sou esse autor

DOI

10.5151/2594-5327-40567

Downloads

Resumo

OS FERROS FUNDIDOS BRANCOS DE ALTO CROMO SãO UTILIZADOS EM OPERAçõES QUE EXIGEM ELEVADA RESISTêNCIA AO DESGASTE. ESTA PROPRIEDADE é ATINGIDA POR UMA MICROESTRUTURA CONSTITUíDA DE UMA REDE DE CARBONETOS EUTéTICOS DO TIPO M7C3 (CR7C3) ALIADA AO TRATAMENTO TéRMICO DE TêMPERA E REVENIMENTO DA MATRIZ. ESTE TRABALHO APRESENTA UMA ANáLISE DA INFLUêNCIA DOS PARâMETROS DE TRATAMENTO TéRMICO NA RESPOSTA à TêMPERA E POSTERIOR REVENIMENTO. PARA TANTO FOI UTILIZADA A ANáLISE DE EQUILíBRIO DE FASES POR THERMOCALC ®, DETERMINAçãO DA CAPACIDADE DE ENDURECIMENTO POR MEDIDAS DE DUREZA ROCKWELL “C” E IDENTIFICAçãO E QUANTIFICAçãO DE FASES POR DIFRAçãO DE RAIOS-X E FERRITOSCóPIO. OS RESULTADOS MOSTRAM QUE A DUREZA NA TêMPERA ATINGE SEU VALOR MáXIMO PARA A AUSTENITIZAçãO A 950ºC, DETERMINADO POR UMA COMBINAçãO ENTRE CAPACIDADE DE ENDURECIMENTO DA MARTENSITA PELO TEOR DE CARBONO DISSOLVIDO NA MATRIZ E PELA FRAçãO DE AUSTENITA RETIDA. NO REVENIMENTO O PICO DE ENDURECIMENTO SECUNDáRIO SE SITUA PRóXIMO DE 500ºC. COM ESTE CONJUNTO DE RESULTADOS é POSSíVEL ESPECIFICAR O MELHOR CICLO DE TRATAMENTO TéRMICO PARA APLICAçõES ESPECíFICAS.

HIGH CHROMIUM WHITE CAST IRONS ARE USED IN OPERATIONS THAT REQUIRE HIGH WEAR RESISTANCE. THIS PROPERTY IS ACHIEVED BY A MICROSTRUCTURE COMPRISING A NETWORK OF EUTECTIC CARBIDES OF THE M7C3 (CR7C3) TYPE, COMBINED WITH THE POSSIBILITY OF HEAT TREATMENT BY QUENCHING AND TEMPERING. THIS WORK ANALYSIS THE HEAT TREATMENT PARAMETERS ON THE RESPONSE TO QUENCHING AND TEMPERING. FOR THIS PURPOSE, PHASE EQUILIBRIUM ANALYSIS WAS USED USING THERMOCALC ®, HARDENING CAPACITY WAS DETERMINED USING ROCKWELL “C” MEASUREMENTS AND PHASES WERE IDENTIFIED AND QUANTIFIED USING X-RAY DIFFRACTION AND A FERRITOSCOPE. THE RESULTS SHOWED THAT THE MAXIMUM MATRIX HARDENING IS REACHED AFTER AUSTENITIZATION AT 950ºC, AS CONSEQUENCE OF THE HARDENING CAPACITY OF MARTENSITE BY THE CARBON CONTENT DISSOLVED IN THE MATRIX AND THE LOWEST RETAINED AUSTENITE FRACTION. DURING TEMPERING, THE SECONDARY HARDENING PEAK IS CLOSE TO 500ºC. THIS SET OF RESULTS ALLOWED THE SPECIFICATION OF THE BEST HEAT TREATMENT CYCLE FOR SPECIFIC APPLICATIONS.

Palavras-chave

Ferro fundido branco; Têmpera; Revenimento; Endurecimento.

White cast iron; Quenching; Tempering; Hardening.