Título

ROCHAS ARTIFICIAIS PRODUZIDAS COM RESÍDUOS DE ESPELHO E DE GRANITO EM MATRIZ POLIMÉRICA COM VARIAÇÕES DA COMPOSIÇÃO GRANULOMÉTRICA E DA PRESSÃO DE COMPACTAÇÃO

ARTIFICIAL STONES PRODUCED WITH MIRROR AND GRANITE WASTE IN A POLYMER MATRIX WITH VARIATIONS IN GRANULOMETRIC COMPOSITION AND COMPACTION PRESSURE

DOI

10.5151/2594-5327-40530

Downloads

Baixar Artigo 1 Downloads

Resumo

A GESTãO ADEQUADA DE RESíDUOS INDUSTRIAIS é UMA PREOCUPAçãO ESSENCIAL DEVIDO AO POTENCIAL POLUENTE E AOS IMPACTOS AMBIENTAIS QUE PODEM CAUSAR. CONSEQUENTEMENTE, Há UM CRESCENTE INTERESSE EM ESTUDAR A APLICAçãO DE RESíDUOS PARA DESENVOLVER NOVOS MATERIAIS. SENDO ASSIM, O OBJETIVO DESTA PESQUISA FOI PRODUZIR PLACAS DE ROCHAS ARTIFICIAIS, USANDO RESíDUOS DE ESPELHO E RESíDUOS DE GRANITO EM MATRIZ EPóXI E ANALISAR SUAS PROPRIEDADES A PARTIR DE VARIAçõES DA COMPOSIçãO GRANULOMéTRICA E DA PRESSãO DE COMPACTAçãO DURANTE SEU PROCESSO DE FABRICAçãO PELA METODOLOGIA DE VIBRAçãO, COMPRESSãO E VáCUO. AS PLACAS PRODUZIDAS FORAM CARACTERIZADAS POR MEIO DOS TESTES DE RESISTêNCIA à FLEXãO EM 3 PONTOS, DETERMINAçãO DA DENSIDADE APARENTE, POROSIDADE APARENTE E ABSORçãO DE áGUA, ALéM DA ANáLISE DA MICROESTRUTURA. COM BASE NOS DADOS ANALISADOS, DENTRE AS ROCHAS TESTADAS, OBSERVOU-SE QUE A ROCHA RGE7-C OBTEVE AS MELHORES PROPRIEDADES, COM DENSIDADE APARENTE DE 2,22 G/CM³, POROSIDADE APARENTE DE 0,25%, ABSORçãO DE áGUA DE 0,11% E RESISTêNCIA à FLEXãO DE 34,36 MPA. ALéM DISSO, AS ROCHAS ANALISADAS TIVERAM DESEMPENHO COERENTE AOS ESTUDOS Já REALIZADOS NA áREA, PERMITINDO SUA UTILIZAçãO NA CONSTRUçãO CIVIL.

 

PROPER MANAGEMENT OF INDUSTRIAL WASTE IS AN ESSENTIAL CONCERN DUE TO THE POLLUTING POTENTIAL AND ENVIRONMENTAL IMPACTS IT CAN CAUSE. CONSEQUENTLY, THERE IS A GROWING INTEREST IN STUDYING THE APPLICATION OF WASTE TO DEVELOP NEW MATERIALS. THEREFORE, THE OBJECTIVE OF THIS RESEARCH WAS TO PRODUCE ARTIFICIAL STONE PLATES, USING MIRROR RESIDUES AND GRANITE RESIDUES IN AN EPOXY MATRIX AND ANALYZE THEIR PROPERTIES BASED ON VARIATIONS IN GRANULOMETRIC COMPOSITION AND COMPACTION PRESSURE DURING THEIR MANUFACTURING PROCESS USING VIBRATION, COMPRESSION AND VACUUM. THE PLATES PRODUCED WERE CHARACTERIZED THROUGH 3-POINT FLEXURAL STRENGTH TESTS, DETERMINATION OF APPARENT DENSITY, APPARENT POROSITY AND WATER ABSORPTION, IN ADDITION TO MICROSTRUCTURE ANALYSIS. BASED ON THE DATA ANALYZED, AMONG THE ROCKS TESTED, IT WAS OBSERVED THAT THE ROCK RGE7-C OBTAINED THE BEST PROPERTIES, WITH AN APPARENT DENSITY OF 2.22 G/CM³, APPARENT POROSITY OF 0.25%, WATER ABSORPTION OF 0. 11% AND FLEXURAL STRENGTH OF 34.36 MPA. FURTHERMORE, THESE ROCKS PERFORMED IN LINE WITH STUDIES ALREADY CARRIED OUT IN THE AREA, ALLOWING THEIR USE IN CIVIL CONSTRUCTION.

Palavras-chave

Rochas artificiais; Resíduo de granito; Resíduo de espelho; Resina epóxi.

Artificial stone; Granite waste; Mirror waste; Epoxy resin.

Como citar

SILVA, THAÍS LEAL DA CRUZ; REIS, MARCELO BARCELLOS; COSTA, ELAINE APARECIDA SANTOS CARVALHO; VIEIRA, CARLOS MAURÍCIO FONTES. ROCHAS ARTIFICIAIS PRODUZIDAS COM RESÍDUOS DE ESPELHO E DE GRANITO EM MATRIZ POLIMÉRICA COM VARIAÇÕES DA COMPOSIÇÃO GRANULOMÉTRICA E DA PRESSÃO DE COMPACTAÇÃO , p. 509-519. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.