SÍNTESE DO CARBONETO DE NIÓBIO ATRAVÉS DE UMA
TÉCNICA DE METALURGIA DO PÓ DE MOAGEM DE ALTA
ENERGIA: SYNTHESIS OF NIOBIUM CARBIDE BY A HIGH ENERGY MILLING TECHNIQUE
OF POWDER METALLURGY

Antonello, Rodrigo Tecchio; Filho, Oscar Olimpio de Araujo; Gonzalez, Cezar Henrique; Filho, Severino Leopoldino Urtiga; Filho, Francisco Ambrozio

doi:10.5151/2594-5327-21426

Anais do Congresso Anual da ABM

ISSN 2594-5327

67º Congresso da ABM - Internacional / 12º ENEMET - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas — vol. 67, num.67 (2012)

Título

SÍNTESE DO CARBONETO DE NIÓBIO ATRAVÉS DE UMA TÉCNICA DE METALURGIA DO PÓ DE MOAGEM DE ALTA ENERGIA

SYNTHESIS OF NIOBIUM CARBIDE BY A HIGH ENERGY MILLING TECHNIQUE OF POWDER METALLURGY

DOI

10.5151/2594-5327-21426

Downloads

Baixar Artigo 220 Downloads

Resumo

O objetivo deste trabalho é obter e caracterizar o carboneto de nióbio (NbC) através de uma técnica de moagem de alta energia que utiliza um tipo de moinho vibratório SPEX, pós elementares de nióbio e de carbono na forma de grafite. Uma vez que, este carboneto é escasso no mercado nacional e é necessário aplicar o NbC como reforço de dois aços rápidos ao molibdênio (AISI M2 e AISI M3:2) objetos de um outro trabalho motivou esta pesquisa. Os pós foram submetidos a um processo de moagem de alta energia com tempos e condições adequados e em seguida, foram caracterizados por meio de Microscopia Eletrônica de Varredura (MEV), Espectroscopia de Energia Dispersiva de raios X (EDS) e Difração de raios X (DRX). O poder de moagem ou relação massa de bola/massa de pós utilizada foi de 10:1. As amostras analisadas mostraram que a moagem de alta energia é uma rota alternativa para a síntese do NbC.

The aim of this work is to obtain and characterize the Niobium Carbide (NbC) by a suitable high energy milling technique using a SPEX Mill vibratory type and niobium and carbon (graphite) powders. Since this carbide is scarced in the national market and it’s necessary to apply this NbC as a reinforcement in two molybdenum high speed steels (AISI M2 and AISI M3:2) object of another work motivated this research. The powders were submitted to a high energy milling procedure for suitable times and conditions and then were characterized by means of Scanning Electronic Microscopy (SEM), Energy Dispersive Spectroscopy (EDS) and X-ray diffraction (DRX) techniques. The ball-to-powder weight ratio was 10:1. The analysed samples showed that the high-energy milling is an alternative route of the NbC synthesis.

Palavras-chave

Metalurgia do pó; Carboneto de nióbio; Moagem de alta energia.

Powder metallurgy; Niobium carbide; High energy milling.

Como citar

Antonello, Rodrigo Tecchio; Filho, Oscar Olimpio de Araujo; Gonzalez, Cezar Henrique; Filho, Severino Leopoldino Urtiga; Filho, Francisco Ambrozio. SÍNTESE DO CARBONETO DE NIÓBIO ATRAVÉS DE UMA TÉCNICA DE METALURGIA DO PÓ DE MOAGEM DE ALTA ENERGIA , p. 3237-3245. In: 67º Congresso da ABM - Internacional / 12º ENEMET - Encontro Nacional de Estudantes de Engenharia Metalúrgica, de Materiais e de Minas, Rio de Jabeiro, 2012.