TENSILE BEHAVIOUR OF EPOXY COMPOSITES REINFORCED WITH ALIGNED PIASSAVA FIBERS

TENSILE BEHAVIOUR OF EPOXY COMPOSITES REINFORCED WITH ALIGNED PIASSAVA FIBERS

Autoria

Nascimento, Denise Cristina Oliveira; Lopes, Felipe Perisse Duarte; Monteiro, Sergio Neves

Nascimento, Denise Cristina Oliveira

Eu sou esse autor

Lopes, Felipe Perisse Duarte

Eu sou esse autor

Monteiro, Sergio Neves

Eu sou esse autor

DOI

10.5151/2594-5327-32364

Downloads

Resumo

The fibers extracted from the piassava palm tree, scientifically known as Attalea funifera, are among the stiffest lignocellulosic fibers being considered for polymer composite reinforcement. Characterization of piassava composites have been carried out for different polymeric matrices and mechanical tests. In this work the tensile properties of DGEBA/TETA epoxy matrix composites reinforced with up to 30% in volume of continuous and aligned piassava fibers were evaluated. Tensile specimens post-cured at 60oC for 4 hours were room temperature tested and the corresponding fracture analyzed by scanning electrons microscopy. The results showed a decrease in both the tensile strength and the elastic modulus of the composites up to 30% with an increase at 40% of piassava fibers to values above those of the pure epoxy. The fracture analysis revealed a weak fiber/matrix interface, which could account for the comparative low performance of these composite in tensile tests up to 30% of volume fraction. The relatively large amount of stronger piassava fibers accounts for the better performance of the composite with 40% in volume fraction.

The fibers extracted from the piassava palm tree, scientifically known as Attalea funifera, are among the stiffest lignocellulosic fibers being considered for polymer composite reinforcement. Characterization of piassava composites have been carried out for different polymeric matrices and mechanical tests. In this work the tensile properties of DGEBA/TETA epoxy matrix composites reinforced with up to 30% in volume of continuous and aligned piassava fibers were evaluated. Tensile specimens post-cured at 60oC for 4 hours were room temperature tested and the corresponding fracture analyzed by scanning electrons microscopy. The results showed a decrease in both the tensile strength and the elastic modulus of the composites up to 30% with an increase at 40% of piassava fibers to values above those of the pure epoxy. The fracture analysis revealed a weak fiber/matrix interface, which could account for the comparative low performance of these composite in tensile tests up to 30% of volume fraction. The relatively large amount of stronger piassava fibers accounts for the better performance of the composite with 40% in volume fraction.

Palavras-chave

Piassava fibers, Epoxy composites, Tensile properties, fracture analysis.

Piassava fibers, Epoxy composites, Tensile properties, fracture analysis.