TESTES DE IMPACTO CHARPY EM COMPÓSITOS DE MATRIZ EPÓXI COM 0,5 VOL.% DE ÓXIDO DE GRAFENO (GO) REFORÇADOS COM TECIDO DE RAMI

CHARPY IMPACT TESTS ON EPOXY MATRIX COMPOSITES WITH 0.5 VOL.% OF GRAPHENE OXIDE (GO) REINFORCED WITH RAMIE FABRIC

Autoria

Pereira, Artur Camposo; Lima, Andreza Menezes; Demosthenes, Luana Cristyne da Cruz; Oliveira, Michelle Souza; Costa, Ulisses Oliveira; Pinheiro, Wagner Anacleto; Monteiro, Sergio Neves

DOI

10.5151/2594-5327-34221

Downloads

Baixar Artigo 13 Downloads

Resumo

O OBJETIVO DESTE TRABALHO FOI INVESTIGAR O COMPORTAMENTO DE TENACIDADE DE COMPÓSITOS DE MATRIZ EPÓXI REFORÇADOS COM ATÉ 30% EM VOLUME DE TECIDO DE RAMI COM 0,5% EM VOLUME DE ÓXIDO DE GRAFENO (GO), POR MEIO DE TESTES DE IMPACTO DE CHARPY. A ADIÇÃO DE GO RESULTA EM UMA MELHORIA VISÍVEL NA CAPACIDADE DE ABSORÇÃO DE ENERGIA DOS COMPÓSITOS. A OBSERVAÇÃO MACROSCÓPICA DAS AMOSTRAS PÓS-IMPACTADAS E A ANÁLISE DE FRATURAS POR MEV DEMONSTRARAM QUE A RUPTURA LONGITUDINAL ATRAVÉS DA INTERFACE DA FIBRA DE RAMI COM A MATRIZ EPÓXI É O PRINCIPAL MECANISMO PARA A MAIOR TENACIDADE ATENDIDA POR ESSES COMPÓSITOS. ALÉM DISSO, VERIFICOU-SE MELHOR ADESÃO ENTRE A FIBRA DE RAMI COM A MATRIZ EPÓXI DEVIDO A INCORPORAÇÃO DO GO.

 

THE OBJECTIVE OF THIS WORK WAS TO INVESTIGATE THE TOUGHNESS BEHAVIOUR OF EPOXY MATRIX COMPOSITES REINFORCED WITH UP TO 30% BY VOLUME OF RAMIE FABRIC WITH 0.5% VOL. GRAPHENE OXIDE (GO), THROUGH CHARPY IMPACT TESTS. THE ADDITION OF GO RESULTS IN A VISIBLE IMPROVEMENT IN THE ENERGY ABSORPTION CAPACITY OF THE COMPOSITES. THE MACROSCOPIC OBSERVATION OF POST-IMPACTED SAMPLES AND THE ANALYSIS OF FRACTURES BY SEM SHOWED THAT THE LONGITUDINAL RUPTURE THROUGH THE INTERFACE OF THE RAMIE FIBER WITH THE EPOXY MATRIX IS THE MAIN MECHANISM FOR THE GREATER TOUGHNESS SERVED BY THESE COMPOSITES. IN ADDITION, IT FOUND BETTER ADHESION BETWEEN THE RAMIE FIBER AND THE EPOXY MATRIX DUE TO THE INCORPORATION OF GO.

Palavras-chave

Matriz epóxi; Charpy; Tecido de rami; Óxido de grafeno, Compósito, Fibra natural.

Epoxy matrix; Ramie fabric; Graphene oxide, Composite, Natural fiber.