TESTES DE IMPACTO IZOD EM COMPÓSITOS DE MATRIZ EPÓXI COM 0,5 VOL.% DE ÓXIDO DE GRAFENO (GO) REFORÇADOS COM TECIDO DE RAMI

IZOD IMPACT TESTS ON EPOXY MATRIX COMPOSITES WITH 0.5 VOL.% OF GRAPHENE OXIDE (GO) REINFORCED WITH RAMIE FABRIC

Autoria

Pereira, Artur Camposo; Lima, Andreza Menezes; Demosthenes, Luana Cristyne da Cruz; Oliveira, Michelle Souza; Costa, Ulisses Oliveira; Pinheiro, Wagner Anacleto; Monteiro, Sergio Neves

DOI

10.5151/2594-5327-34222

Downloads

Baixar Artigo 13 Downloads

Resumo

O ÓXIDO DE GRAFENO (GO) FOI UTILIZADO PARA MELHORIAS DAS PROPRIEDADES DE COMPÓSITOS POLÍMEROS. COMPÓSITOS DE MATRIZ DE EPÓXI COM TECIDO DE RAMI (BOEHMERIA NIVEA) JÁ OBTÉM DESTAQUES TECNOLÓGICOS DEVIDO SEUS BONS RESULTADOS MECÂNICOS. O OBJETIVO DESTE TRABALHO FOI INVESTIGAR O COMPORTAMENTO DE TENACIDADE DE COMPÓSITOS DE MATRIZ EPÓXI COM 0,5 VOL.% DE ÓXIDO DE GRAFENO (GO), REFORÇADOS COM 30% EM VOLUME DE TECIDO DE RAMI POR MEIO DE TESTES DE IMPACTO DE IZOD. A ADIÇÃO DE GO RESULTA EM UMA MELHORIA VISÍVEL NA CAPACIDADE DE ABSORÇÃO DE ENERGIA DOS COMPÓSITOS. A OBSERVAÇÃO MACROSCÓPICA DAS AMOSTRAS PÓS-IMPACTADAS E A ANÁLISE DAS FRATURAS POR MEV, MOSTRARAM QUE A RUPTURA LONGITUDINAL ATRAVÉS DA INTERFACE DA FIBRA DE RAMI COM A MATRIZ EPÓXI, É O PRINCIPAL MECANISMO PARA A MAIOR TENACIDADE ATENDIDA POR ESSES COMPÓSITOS. ALÉM DISSO, VERIFICOU-SE MELHOR ADESÃO ENTRE A FIBRA DE RAMI COM A MATRIZ EPÓXI DEVIDO A INCORPORAÇÃO DO GO.

 

THE GRAPHENE OXIDE (GO) WAS USED TO IMPROVE THE PROPERTIES OF POLYMER COMPOUNDS. THE EPOXY MATRIX COMPOUNDS WITH RAMIE FABRIC (BOEHMERIA NIVEA) ALREADY OBTAIN THESE TECHNOLOGICAL TECHNIQUES DUE TO THEIR GOOD MECHANICAL RESULTS. THE OBJECTIVE OF THIS WORK WAS TO INVESTIGATE THE TOUGHNESS BEHAVIOR OF EPOXY MATRIX COMPOUNDS WITH 0.5% GO, REINFORCED WITH 30% BY VOLUME OF RAMIE FABRIC BY IZOD IMPACT TESTS. THE ADDITION OF GO RESULTS IN A VISIBLE IMPROVEMENT IN THE ENERGY ABSORPTION CAPACITY OF THE COMPOUNDS. A MACROSCOPIC OBSERVATION OF POST-IMPACTED SAMPLES AND AN ANALYSIS OF FRACTURES BY SEM SHOWS THAT A LONGITUDINAL RUPTURE THROUGH THE RAMIE FIBER INTERFACE WITH AN EPOXY MATRIX IS THE MAIN MECHANISM FOR A GREATER TOUGHNESS SERVED BY THESE COMPOSITES. IN ADDITION, THERE WAS A BETTER ADHESION BETWEEN A RAMIE FIBER AND AN EPOXY MATRIX DUE TO THE INCORPORATION OF GO.

Palavras-chave

Matriz epóxi; Izod; Tecido de rami; Óxido de grafeno, Compósito, Fibra natural.

Epoxy matrix; Izod; Ramie fabric; Graphene oxide, Composite, Natural fiber.