TEXTURIZAÇÃO A LASER: EFEITO DO FEIXE DE LASER NA RUGOSIDADE E NA MOLHABILIDADE DE SUPERFÍCIES DE COBRE ELETROLÍTICO

LASER TEXTURING: EFFECT OF LASER BEAM ON ROUGHNESS AND WETTABILITY OF ELECTROLYTIC COPPER SURFACES

Autoria

CARVALHO, SHEILA MEDEIROS DE; LIMA, MILTON SÉRGIO FERNANDES DE; LUBE, REBECA OLIVEIRA; DELLATORRE, ENZA DE SOUZA ZANON

CARVALHO, SHEILA MEDEIROS DE

Eu sou esse autor

LIMA, MILTON SÉRGIO FERNANDES DE

Eu sou esse autor

LUBE, REBECA OLIVEIRA

Eu sou esse autor

DELLATORRE, ENZA DE SOUZA ZANON

Eu sou esse autor

DOI

10.5151/2594-4711-40493

Downloads

Resumo

O PRESENTE TRABALHO VISA CONTRIBUIR COM O ENTENDIMENTO DOS FENôMENOS ENVOLVIDOS NO CARáTER BIOCIDA DE SUPERFíCIES TEXTURIZADAS DE CHAPAS DE COBRE ELETROLíTICO DE 1 MM DE ESPESSURA. DENTRE AS DIVERSAS FORMAS DE MODIFICAçãO DE SUPERFíCIE, A TEXTURIZAçãO A LASER TORNA-SE UMA ALTERNATIVA VIáVEL, POIS PROMOVE A MODIFICAçãO SUPERFICIAL NO MATERIAL, MANTENDO AS PROPRIEDADES DO VOLUME INALTERADAS. O EQUIPAMENTO UTILIZADO PARA A TEXTURIZAçãO FOI UM LASER A FIBRA DE 50 W DE POTêNCIA, OPERANDO NO REGIME PULSADO, FREQUêNCIA DE 50 KHZ E A UMA VELOCIDADE DE ESCANEAMENTO DE 5 MM/S. VERIFICOU-SE QUE A AçãO DO LASER NA SUPERFíCIE DO MATERIAL PROMOVEU ALTERAçõES NA TOPOGRAFIA, UMA VEZ QUE OS VALORES DE RUGOSIDADE, RA E RQ, NO MATERIAL TEXTURIZADO AUMENTOU EM MAIS DE 3 VEZES, EM COMPARAçãO COM O MATERIAL COMO RECEBIDO. EMBORA O LASER TENHA ALTERADO AS CARACTERíSTICAS TOPOGRáFICAS E DE RUGOSIDADE, A DIFRATOMETRIA DE RAIOS-X MOSTROU QUE NãO HOUVE ALTERAçõES NA ESTRUTURA CRISTALINA DO COBRE.

THE PRESENT WORK AIMS TO CONTRIBUTE TO THE UNDERSTANDING OF THE PHENOMENA INVOLVED IN THE BIOCIDAL NATURE OF TEXTURED SURFACES OF 1 MM THICK ELECTROLYTIC COPPER SHEETS. AMONG THE VARIOUS FORMS OF SURFACE MODIFICATION, LASER TEXTURING BECOMES A VIABLE ALTERNATIVE, AS IT PROMOTES SURFACE MODIFICATION IN THE MATERIAL, KEEPING THE VOLUME PROPERTIES UNCHANGED. THE EQUIPMENT USED FOR TEXTURING WAS A 50 W FIBER LASER, OPERATING IN A PULSED REGIME, FREQUENCY OF 50 KHZ AND A SCANNING SPEED OF 5 MM/S. IT WAS FOUND THAT THE LASER ACTION ON THE SURFACE OF THE MATERIAL PROMOTED CHANGES IN THE TOPOGRAPHY, SINCE THE ROUGHNESS VALUES, RA AND RQ, IN THE TEXTURED MATERIAL INCREASED BY MORE THAN 3 TIMES, COMPARED TO THE AS RECEIVED MATERIAL. ALTHOUGH THE LASER CHANGED THE TOPOGRAPHIC AND ROUGHNESS CHARACTERISTICS, X-RAY DIFFRACTOMETRY SHOWED THAT THERE WERE NO CHANGES IN THE CRYSTALLINE STRUCTURE OF THE COPPER.

Palavras-chave

Texturização a laser; Cobre eletrolítico; Rugosidade.

Laser surface texturing; Electrolytical copper; Roughness.